Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | ISO294-4 | 0.40to0.70 | % |
Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 31.0 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | | ISO2039-1 | 105 | Mpa |
Tensile Stress | Yield,23°C | ISO527-2 | 46.0 | Mpa |
Tensile Strain | Yield,23°C | ISO527-2 | 2.6 | % |
Tensile Strain | Break,23°C | ISO527-2 | >15 | % |
Tensile Modulus | | ISO527-2 | 2400 | Mpa |
Flexural Modulus | | ISO178 | 2400 | Mpa |
Flexural Stress | | ISO178 | 70.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ISO306/B50 | 99.0 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 9E-05 | cm/cm/°C |
Heat Deflection Temperature | 0.45MPa,Annealed | ISO75-2/B | 98.0 | °C |
Heat Deflection Temperature | 1.8MPa,Annealed | ISO75-2/A | 94.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Electric strength | 1.50mm | IEC60243-1 | 35 | KV/mm |
Dissipation Factor? | 100Hz | IEC60250 | 5E-03 | |
Dissipation Factor? | 1MHz | IEC60250 | 9E-03 | |
Relative Permittivity | 100Hz | IEC60250 | 3.00 | |
Relative Permittivity | 1MHz | IEC60250 | 2.90 | |
Comparative Tracking Index | | IEC60112 | 600 | V |
Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179 | 90 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179 | 110 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.