ABS TAITALAC® 5000M TAIDA TAIWAN
130
- Unit Price:
- $1577 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 19MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity High gloss Impact resistance High gloss hard Impact resistance High rigidity Highlight Moderate impact resistanc
- Application Areas:Household goods Video tape
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | Saturation | ASTM D570 | < 0.30 | % |
| (23°C,24hr) | ASTMD570 | <0.30 | % | |
| Melt Mass-Flow Rate | 200℃/5.0 kg | ASTM D1238 | 1.8 | g/10 min |
| 220℃/10.0 kg | ASTM D1238 | 20 | g/10 min | |
| Modeling Shrinkage | MD | ASTMD995 | <0.40 | % |
| MD | ASTM D955 | < 0.40 | % | |
| Melt Mass-Flow Rate | 200℃/5.0Kg | ASTMD1238 | 1.8 | g/10min |
| 220℃/10.0Kg | ASTMD1238 | 20 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength | Yield, 23℃, 3.18 mm | ASTM D638 | 44.1 | Mpa |
| Break, 23℃, 3.18 mm | ASTM D638 | 37.3 | Mpa | |
| Notched Izod Impact Strength | 23°C | ASTMD256 | 220 | J/m |
| 23℃, 3.18 mm | ASTM D256 | 200 | J/m | |
| 23℃, 6.35 mm | ASTM D256 | 180 | J/m | |
| Tensile Elongation?(Break) | 23°C | ASTMD638 | 30 | % |
| Tensile Strength | 23°C | ASTMD638 | 44 | Mpa |
| Tensile Elongation | Break, 23℃, 3.18 mm | ASTM D638 | 30 | % |
| Rockwell Hardness | R-Scale, 23℃ | ASTM D785 | 115 | |
| Flexural Modulus | 23°C | ASTMD790 | 2550 | Mpa |
| 23℃ | ASTM D790 | 27000 | Mpa | |
| Flexural Strength | 23°C | ASTMD790 | 76 | Mpa |
| Yield, 23℃ | ASTM D790 | 77.5 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8 MPa, Annealed, 12.7 mm | ASTM D648 | 85 | °C |
| 1.80MPaUnannealed | ASTMD648 | 85 | °C | |
| Vicat Softening Temperature | ASTM D1525 | 103 | °C | |
| ASTM1525 | 103 | °C | ||
| Flame Rating | 1.59 mm | UL 94 | HB | |
| High Amp Arc Ignition | 1.57 mm | UL 746 | 200 | |
| High Voltage Arc Tracking Rate | 1.57 mm | UL 746 | 0.00 | mm/min |
| Hot-wire Ignition | 1.57 mm | UL 746 | 18 | sec |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Insulation strength | ASTMD149 | 22 | KV/mm | |
| Volume Resistivity | ASTMD257 | 1E+22 | Ω.cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | ASTMD785 | 115 | R |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Other Prices
| Port of Loading | Unit Price |
|---|---|
| HongKong port, HK China | 1550 USD/MT |