Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | ISO294-4 | 0.40到0.60 | % |
Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 25.0 | cm3/10min |
Density / Specific Gravity | | ISO1183 | 1.05 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Stress | | ISO178 | 72.0 | Mpa |
Tensile Stress | Yield,23°C | ISO527-2 | 47.0 | Mpa |
Tensile Strain | Yield,23°C | ISO527-2 | 2.5 | % |
Tensile Strain | Break,23°C | ISO527-2 | >15 | % |
Tensile Modulus | | ISO527-2 | 2400 | Mpa |
Flexural Modulus | | ISO178 | 2400 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ISO306/B50 | 101 | °C |
Heat Deflection Temperature | 0.45MPa,Annealed | ISO75-2/B | 102 | °C |
Heat Deflection Temperature | 1.8MPa,Annealed | ISO75-2/A | 98.0 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 8E-05 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | 1.50mm | IEC60243-1 | 33 | KV/mm |
Relative Permittivity | 100Hz | IEC60250 | 3.10 | |
Relative Permittivity | 1MHz | IEC60250 | 3.00 | |
Comparative Tracking Index | | IEC60112 | 600 | V |
Dissipation Factor? | 100Hz | IEC60250 | 5E-03 | |
Dissipation Factor? | 1MHz | IEC60250 | 8E-03 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179 | 80 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179 | 90 | kJ/m² |
Charpy Notched Impact Strength | -30°C | ISO179 | 7.0 | kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO179 | 17 | kJ/m² |
Notched Izod Impact Strength | -30°C | ISO180/A | 7.0 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/A | 17 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | | ISO2039-1 | 105 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.