Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting
- Application Areas:Electrical/Electronic App Electrical field Electronic field Automotive sector Automotive interior parts Automotive External Parts Shell
- Color:--
- Grade:Heat resistant grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTMD955 | 0.40to0.70 | % |
| MD：3.20mm | ISO294-4 | 0.40to0.70 | % | |
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 7.0 | g/10min |
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 7.00 | cm3/10min |
| Density/specific gravity | ASTMD792 | 1.05 | g/cm³ | |
| ISO1183 | 1.05 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2/1 | 2450 | Mpa | |
| Bending modulus 4 | ISO178 | 2550 | Mpa | |
| Bending modulus 3 | 3.20mm | ASTMD790 | 2650 | Mpa |
| Tensile strength 2 | Yield,3.20mm | ASTMD638 | 52.0 | Mpa |
| Elongation rate 2 | Break,3.20mm | ASTMD638 | 20 | % |
| Bending stress 4 | ISO178 | 82.0 | Mpa | |
| Tensile stress | Yield | ISO527-2/50 | 54.0 | Mpa |
| FlexuralStrength3 | 3.20mm | ASTMD790 | 84.3 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 5 | 0.45MPa,Unannealed,4.00mm | ISO75-2/Be | 101 | °C |
| 1.8MPa,Unannealed,4.00mm | ISO75-2/Ae | 93.0 | °C | |
| RTIElec | UL746 | 60.0 | °C | |
| Evolution Calendar intelligent importer | UL746 | 60.0 | °C | |
| RTIStr | UL746 | 60.0 | °C | |
| Linear coefficient of thermal expansion | MD：23to60°C | ISO11359-2 | 8.0E-5to9.0E-5 | cm/cm/°C |
| TD：23to60°C | ISO11359-2 | 8.0E-5to9.0E-5 | cm/cm/°C | |
| Vicat softening temperature | ASTMD15256 | 112 | °C | |
| ISO306/B50 | 112 | °C | ||
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 111 | °C |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 102 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Arc resistance | ASTMD495 | PLC6 | ||
| Volume resistivity | 23°C | ASTMD257 | 1.5E+03 | ohms·cm |
| Dielectric strength | 23°C,1.00mm | ASTMD149 | 33 | KV/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 6.0 | kJ/m² |
| 23°C | ISO179/1eA | 12 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C,3.20mm | ASTMD256 | 59 | J/m |
| -30°C,6.40mm | ASTMD256 | 49 | J/m | |
| 23°C,3.20mm | ASTMD256 | 160 | J/m | |
| 23°C,6.40mm | ASTMD256 | 140 | J/m | |
| -30°C | ISO180/1A | 6.0 | kJ/m² | |
| 23°C | ISO180/1A | 13 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | ISO2039-2 | 114 | ||
| R-Scale | ASTMD785 | 112 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.