Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | ASTMD955 | 0.55 | % |
Modeling Shrinkage | | ISO294-4 | 0.40to0.70 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.25 | % |
Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 7.0 | g/10min |
Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 7.00 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | | ISO2039-1 | 102 | Mpa |
Nominal Tensile Strain at Break | 23°C | ISO527-2 | 9.0 | % |
Tensile Stress | Yield,23°C | ISO527-2 | 51.0 | Mpa |
Tensile Strain | Yield,23°C | ISO527-2 | 3.0 | % |
Tensile Strength | Yield,23°C | ASTMD638 | 52.0 | Mpa |
Flexural Stress | | ISO178 | 72.0 | Mpa |
Tensile Modulus | | ASTMD638 | 2500 | Mpa |
Tensile Modulus | | ISO527-2 | 2400 | Mpa |
Tensile Elongation | Break | ASTMD638 | 3.0 | % |
Flexural Modulus | | ASTMD790 | 2400 | Mpa |
Flexural Modulus | | ISO178 | 2400 | Mpa |
Flexural Strength | | ASTMD790 | 77.2 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | MD | ISO11359-2 | 9E-05 | cm/cm/°C |
Vicat Softening Temperature | -- | ISO306/A50 | 115 | °C |
Vicat Softening Temperature | -- | ISO306/B50 | 106 | °C |
Maximum Service Temperature | | | 85 | °C |
Heat Deflection Temperature | 0.45MPa,Annealed | ISO75-2/B | 107 | °C |
Heat Deflection Temperature | 1.8MPa,Annealed | ISO75-2/A | 99.0 | °C |
Thermal Conductivity | | DIN52612 | 0.17 | W/m/K |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Comparative Tracking Index | | IEC60112 | 600 | V |
Electric strength | 1.50mm | IEC60243-1 | 39 | KV/mm |
Volume Resistivity | | ASTMD257 | >1.0E+15 | ohms·cm |
Volume Resistivity | | IEC60093 | 1E+15 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179 | 100 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179 | 190 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.