Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD2.0mm | ISO294-4 | 0.55 | % |
Moisture Absorption | (23°C,24hr) | ISO62 | 0.95 | % |
Moisture Absorption | (23°C,50RH) | ISO62 | 0.24 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 130 | kJ/m² |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 90 | kJ/m² |
Tensile Elongation?(Break) | 23°C | ISO527-2 | 2.4 | % |
Tensile Modulus | 23°C | ISO527-2 | 2300 | Mpa |
Flexural Strength | 23°C | ISO178 | 65 | Mpa |
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 19 | kJ/m² |
Charpy Notched Impact Strength | -30°C | ISO179/1eA | 7 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/1A | 22 | kJ/m² |
Notched Izod Impact Strength | -30°C | ISO180/1A | 7 | kJ/m² |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ISO306/A50 | 102 | °C |
Vicat Softening Temperature | | ISO306/B50 | 95 | °C |
Deflection Temperature Under Load? | 0.45MPaAnnealed | ISO75-2/B | 95 | °C |
Deflection Temperature Under Load? | 1.80MPaAnnealed | ISO75-2/A | 92 | °C |
Coefficient of Linear Thermal Expansion | 导热系数 | DIN52612 | 0.17 | W/m/K |
Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 8E-05 | cm/cm/°C |
Coefficient of Linear Thermal Expansion | TD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Volume Resistivity | | IEC60093 | 1E+15 | Ω.cm |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | | ISO2039-1 | 99 | Mpa |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
The Yellow Index | | DIN6167 | 15 | YI |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.