ABS P2H-AT ELIX POLYMERS SPANISH
133
- Unit Price:
- $2327 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 60MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Glass fiber reinf 16% filler by weight
- Application Areas:Application in the automo
- Color:--
- Grade:Anti static level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO294-4 | 0.40to0.60 | % |
| MD | ISO294-4 | 0.40to0.60 | % | |
| Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 37.0 | cm3/10min |
| Density | ISO1183 | 1.05 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Creep Modulus | 1000hr | ISO899-1 | 1500 | Mpa |
| Tensile Stress | 屈服,23°C | ISO527-2/50 | 44.0 | Mpa |
| Tensile Strain | 屈服,23°C | ISO527-2/50 | 2.1 | % |
| 断裂,23°C | ISO527-2/50 | >15 | % | |
| Tensile Modulus | 23°C | ISO527-2/1 | 2500 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 2400 | Mpa |
| Flexural Strength | 23°C | ISO178 | 70.0 | Mpa |
| Tensile Creep Modulus | 1hr | ISO899-1 | 2200 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear thermal expansion coefficient | MD：23到55°C | ISO11359-2 | 9E-05 | cm/cm/°C |
| MD：23到55°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| Deflection Temperature Under Load? | 0.45MPa,退火 | ISO75-2/B | 97.0 | °C |
| 1.8MPa,退火 | ISO75-2/A | 93.0 | °C | |
| Vicat Softening Temperature | ISO306/B50 | 98.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+15 | ohms | |
| Volume Resistivity | IEC60093 | 1E+15 | ohms·cm | |
| Dielectric Strength | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
| Comparative Tracking Index | 解决方案A | IEC60112 | 600 | V |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 100 | kJ/m² |
| -30°C | ISO179/1eU | 80 | kJ/m² | |
| -30°C | ISO179/1eU | 80 | kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 7.0 | kJ/m² |
| -30°C | ISO179/1eA | 7.0 | kJ/m² | |
| 23°C | ISO179/1eA | 16 | kJ/m² | |
| 23°C | ISO179/1eA | 16 | kJ/m² | |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 7.0 | kJ/m² |
| 23°C | ISO180/1A | 16 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball Indentation Hardness | ISO2039-1 | 110 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glow Wire Flammability Index | 2.0mm | IEC60695-2-12 | 700 | °C |
| Burning Rate | 2.00mm | ISO3795 | 60 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.