ABS POLYLAC® PA-747S（钛白） TAIWAN CHIMEI

128

Unit Price:
$2190 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility
Application Areas:Home appliance components
Color:--
Grade:Extrusion grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	200°C/5.0kg	ASTMD1238	0.50	g/10min
Melt Volume flow Rate	220°C/10.0kg	ISO1133	2.50	cm3/10min
Density / Specific Gravity	--3	ASTMD792	1.03	g/cm³
Density / Specific Gravity	Density / Specific Gravity	23°C	ISO1183	1.04	g/cm³
Modeling Shrinkage		ISO294-4	0.40到0.70	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength	Yield4	ASTMD638	38.1	Mpa
	Tensile Strength	Yield	ISO527-2/50	41.0	Mpa
	Tensile Strength	Tensile Strength	Break	ISO527-2/50	30.0	Mpa
Tensile Elongation	Break4	ASTMD638	40	%
Tensile Elongation	Tensile Elongation	Break	ISO527-2/50	25	%
Flexural Modulus	--5	ASTMD790	2070	Mpa
Flexural Modulus	Flexural Modulus	--6	ISO178	1700	Mpa
Flexural Strength	--5	ASTMD790	60.7	Mpa
Flexural Strength	Flexural Strength	--6	ISO178	61.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8MPa,Unannealed	ASTMD648	85.0	°C
	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	83.0	°C
		Deflection Temperature Under Load?	1.8MPa,Annealed	ASTMD648	95.0	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Annealed	ISO75-2/A	99.0	°C
Vicat Softening Temperature	--	ASTMD15257	103	°C
	Vicat Softening Temperature	--	ISO306/A50	106	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B50	101	°C
Linear thermal expansion coefficient	MD	ISO11359-2	9.1E-05	cm/cm/°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C	ISO179	28	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179	39	kJ/m²
Notched Izod Impact Strength	23°C,3.20mm	ASTMD256	400	J/m
	Notched Izod Impact Strength	23°C,6.40mm	ASTMD256	350	J/m
		Notched Izod Impact Strength	-30°C	ISO180/1A	26	kJ/m²
		Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	37	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTMD785	102

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.