ABS POLYLAC® D-1000 ZHENJIANG CHIMEI
126
- Unit Price:
- $2603 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 110MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Modeling Shrinkage | ASTM D-55 | 0.3-0.5 | % | |
Density / Specific Gravity | 23℃(73℉) | ASTM D-792 | 1.19 |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Rockwell Hardness | 23℃(73℉) | ASTM D-785 | 101 | R scale |
Tensile Strength | 1/8"Thickness 50mm/min 23℃(73℉) | ASTM D-638 | 435(42.7)(6.18) | kgf/cm2(MPa)(PSI×103) |
Tensile Strength | 1/8"×1"×4"bar 15mm/min 23℃(73℉) | ASTM D-790 | 715(70.1)(10.1) | kgf/cm2(MPa)(PSI×103) |
IZOD Notch Impact Strength | 1/4"bar 23℃(73℉) | ASTM D-256 Method A | 17(167)(3.12) | Kgf-cm/cm(J/M)(ft-1bs/in.) |
1/8"bar 23℃(73℉) | ASTM D-256 Method A | 20(196)(3.7) | Kgf-cm/cm(J/M)(ft-1bs/in.) | |
Tensile Modulus | 1/8"×1"×4"bar 15mm/min 23℃(73℉) | ASTM D-790 | 25535(2.5)(3.63) | Kgf/cm2(GPa)(PSi×105 |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Flame Rating | 1/8"Thickness 2.86mm | UL 94 | 5-VA | |
1/16"Thickness | UL 94 | V-0 | ||
Vicat Softening Temperature | Load 1Kg | ASTM D-1525 | 94(201) | ℃(℉) |
Deflection Temperature Under Load? | 1/2"×1/2"×5"bar 18.6kgf/cm2(264PSi) | ASTM D-648 | 77(171) | ℃(℉) |
Physical | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Melt index | 200℃,5kg | ASTM D-1238 | 4.0 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.