Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 200°C/5.0kg | ASTMD1238 | 0.40 | g/10min |
| Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 4.00 | cm3/10min |
| Modeling Shrinkage | | ISO294-4 | 0.40到0.70 | % |
| Density | --3 | ASTMD792 | 1.03 | g/cm³ |
| Density | 23°C | ISO1183 | 1.03 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | 屈服4 | ASTMD638 | 36.2 | Mpa |
| Tensile Strength | 屈服 | ISO527-2/50 | 37.0 | Mpa |
| Tensile Strength | 断裂 | ISO527-2/50 | 29.0 | Mpa |
| Tensile Elongation | 断裂4 | ASTMD638 | 40 | % |
| Tensile Elongation | 断裂 | ISO527-2/50 | 30 | % |
| Flexural Modulus | --5 | ASTMD790 | 1930 | Mpa |
| Flexural Modulus | --6 | ISO178 | 1500 | Mpa |
| Flexural Strength | --5 | ASTMD790 | 55.2 | Mpa |
| Flexural Strength | --6 | ISO178 | 51.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ASTMD648 | 85.0 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/A | 81.0 | °C |
| Deflection Temperature Under Load? | 1.8MPa,退火 | ASTMD648 | 95.0 | °C |
| Deflection Temperature Under Load? | 1.8MPa,退火 | ISO75-2/A | 96.0 | °C |
| Vicat Softening Temperature | -- | ASTMD15257 | 106 | °C |
| Vicat Softening Temperature | -- | ISO306/A50 | 104 | °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 98.0 | °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 9.5E-05 | cm/cm/°C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179 | 30 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179 | 42 | kJ/m² |
| Notched Izod Impact Strength | 23°C,3.20mm | ASTMD256 | 430 | J/m |
| Notched Izod Impact Strength | 23°C,6.40mm | ASTMD256 | 210 | J/m |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 28 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 40 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.