Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | ASTMD955 | <0.40 | % |
Moisture Absorption | 24hr | ASTMD570 | <0.30 | % |
Melt Mass-Flow Rate | 200°C/5.0kg | ASTMD1238 | 2.0 | g/10min |
Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 20 | g/10min |
Density / Specific Gravity | | ASTMD792 | 1.04 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Strength | Yield,23°C | ASTMD790 | 73.5 | Mpa |
Flexural Modulus | 23°C | ASTMD790 | 2550 | Mpa |
Tensile Strength | Yield,23°C,3.18mm | ASTMD638 | 42.1 | Mpa |
Tensile Elongation | Break,23°C,3.18mm | ASTMD638 | 30 | % |
Tensile Strength | Break,23°C,3.18mm | ASTMD638 | 35.2 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
RTIElec | 1.6mm | UL746 | 60.0 | °C |
Evolution Calendar intelligent importer | 1.6mm | UL746 | 60.0 | °C |
RTIStr | 1.6mm | UL746 | 60.0 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,12.7mm | ASTMD648 | 83.0 | °C |
Vicat Softening Temperature | | ASTMD15254 | 103 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
High Amp Arc Ignition | 1.57mm | UL746 | 200 | |
High Amp Arc Ignition | 1.57mm | UL746 | 0.00 | mm/min |
Hot-wireIgnition | 1.57mm | UL746 | 18 | sec |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | 23°C,3.18mm | ASTMD256 | 200 | J/m |
Notched Izod Impact Strength | 23°C,6.35mm | ASTMD256 | 180 | J/m |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Sale,23°C | ASTMD785 | 115 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 1.6mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.