Material Description

Technical Data Sheet

Material Description

Material Properties:Low warpage Aging resistance Filler: Glass fiber reinf 10% filler by weight
Application Areas:packing Electronic and Electrical
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD1	内部方法	0.30到0.80	%
	Modeling Shrinkage	MD:3.20mm	内部方法	0.40到0.60	%
	Modeling Shrinkage	Modeling Shrinkage	TD2	内部方法	0.50到0.90	%
Moisture Absorption	Saturation,23°C	ISO62	0.15	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.10	%
Melt Mass-Flow Rate	200°C/3.8kg	ASTMD1238	18	g/10min
	Melt Mass-Flow Rate	265°C/5.0kg	ASTMD1238	85	g/10min
	Melt Mass-Flow Rate	Melt Mass-Flow Rate	266°C/5.0kg	ASTMD1238	85	g/10min
Melt Volume flow Rate	250°C/2.16kg	ISO1133	18.0	cm3/10min
	Melt Volume flow Rate	250°C/5.0kg	ISO1133	50.0	cm3/10min
	Melt Volume flow Rate	Melt Volume flow Rate	265°C/5.0kg	ISO1133	75.0	cm3/10min
Density / Specific Gravity		ASTMD792,ISO1183	1.31	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
--		ISO527-2/1	4700	Mpa
--3		ASTMD638	4600	Mpa
yield		ISO527-2/5	95.0	Mpa
yield	yield		ISO527-2/5	3.0	%
fracture		ISO527-2/5	95.0	Mpa
fracture	fracture		ISO527-2/5	3.0	%
Taber Abrasion Resistance	1000Cycles,1000g,CS-17Wheel	内部方法	54.0	mg
Yield		ASTMD638	90.0	Mpa
Break		ASTMD638	90.0	Mpa
Yield		ASTMD638	3.0	%
Break		ASTMD638	3.0	%
50.0mm Span		ASTMD790	3600	Mpa
--9		ISO178	4000	Mpa
--10		ISO178	140	Mpa
--11		ISO178	130	Mpa
Yield,50.0mm Span		ASTMD790	126	Mpa
Flexural Strain (Break)		ISO178	5.0	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
1.8MPa, Unannealed,64.0mm Span		ISO75-2/Af	115	°C
Flow:23 to 150°C		ISO11359-2	3.9E-05	cm/cm/°C
Flow:23 to 150°C		ISO11359-2	1.5E-04	cm/cm/°C
0.45MPa, Unannealed,3.20mm		ASTMD648	175	°C
--		ASTMD1525,ISO306/B50,ISO306/B12025	145	°C
--	--		ASTMD1525,ISO306/A501426	205	°C
Flow:-40 to 40°C		ASTME831	4E-05	cm/cm/°C
Flow:-40 to 40°C	Flow:-40 to 40°C		ISO11359-2	3.7E-05	cm/cm/°C
Flow:23 to 80°C		ISO11359-2	4E-05	cm/cm/°C
Flow:-40 to 40°C		ASTME831	9E-05	cm/cm/°C
Flow:-40 to 40°C	Flow:-40 to 40°C		ISO11359-2	7E-05	cm/cm/°C
Flow:23 to 80°C		ISO11359-2	9E-05	cm/cm/°C
1.8MPa, Unannealed,3.20mm		ASTMD648	115	°C
Ball PressureTest	125°C	IEC60695-10-2	Pass
0.45MPa, Unannealed,3.20mm Span		ISO75-2/Bf	135	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		IEC60093	>1.0E+15	ohms
Volume Resistivity		ASTMD257,IEC60093	>1.0E+15	ohms·cm
High Amp Arc Ignition	HAI	UL746	PLC0
Hot-wire Ignition	HWI	UL746	PLC0
Comparative Tracking Index	--	IEC60112	200	V
Comparative Tracking Index	Comparative Tracking Index	SolutionB	IEC60112	100	V
1MHz		ASTMD150,IEC60250	3.10
1MHz	1MHz		ASTMD150,IEC60250	0.014
100Hz		IEC60250	3.20
100Hz	100Hz		IEC60250	0.016
1.60mm,inOil		ASTMD149	25	KV/mm
3.20mm,inOil		ASTMD149	18	KV/mm
0.800mm, in oil		IEC60243-1	29	KV/mm
1.60mm,in Oil		IEC60243-1	25	KV/mm
3.20mm,in Oil		IEC60243-1	18	KV/mm
50Hz		IEC60250	9E-03
50Hz	50Hz		IEC60250	3.00
60Hz		IEC60250	3.00
60Hz	60Hz		IEC60250	9E-03
0.800mm,inOil		ASTMD149	29	KV/mm

Fill Analysis	Test Condition	Test Method	Test Result	Unit
Melt Viscosity	260°C,1500sec^-1	ISO11443	145	Pa·s

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	37.0	J
23°C		ASTMD256	47	J/m
	23°C		ISO179/2C	6.0	kJ/m²
	23°C	23°C		ASTMD4812	480	J/m
-30°C18		ISO180/1A	5.0	kJ/m²
0°C19		ISO180/1A	5.0	kJ/m²
-30°C21		ISO180/1U	30	kJ/m²
23°C22		ISO180/1U	40	kJ/m²
23°C20		ISO180/1A	6.0	kJ/m²
-30°C16		ISO179/1eU	30	kJ/m²
-30°C		ASTMD256	47	J/m
	-30°C		ISO179/2U	40	kJ/m²
		-30°C		ASTMD4812	470	J/m
		-30°C	-30°C		ISO179/2C	6.0	kJ/m²
0°C		ASTMD256	47	J/m
23°C17		ISO179/1eU,ISO179/2U	40	kJ/m²
23°C15		ISO179/1eA	4.0	kJ/m²
-30°C14		ISO179/1eA	4.0	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Sale	ISO2039-2	122
Ball Indentation Hardness	H358/30	ISO2039-1	165	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.60mm,TestingbySABIC	UL94	HB
Glow Wire Flammability Index	1.00mm	IEC60695-2-12	750	°C
Glow Wire Flammability Index	Glow Wire Flammability Index	3.00mm	IEC60695-2-12	850	°C
Oxygen Index		ISO4589-2	21	%

Supplementary information	Test Condition	Test Method	Test Result	Unit
Filler Content		ASTMD229	10	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.