Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow 2	内部方法	0.060 到 0.080	%
	Modeling Shrinkage	Flow : 3.20 mm	内部方法	0.60 到 0.80	%
	Modeling Shrinkage	Modeling Shrinkage	Across Flow : 3.20 mm	内部方法	0.60 到 0.80	%
Melt Mass-Flow Rate	260°C/5.0 kg	ASTM D1238	16	g/10 min
Melt Volume flow Rate	260°C/5.0 kg	ISO 1133	18.0	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	-- 6, 7	ISO 178	48.0	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 5	ASTM D790	48.0	Mpa
Tensile Modulus	-- 3	ASTM D638	1240	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	1670	Mpa
Tensile Elongation	Yield 4	ASTM D638	10	%
	Tensile Elongation	Yield	ISO 527-2/50	8.2	%
		Tensile Elongation	Break 4	ASTM D638	130	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	120	%
Flexural Modulus	50.0 mm Span 5	ASTM D790	1440	Mpa
Flexural Modulus	Flexural Modulus	-- 6	ISO 178	1600	Mpa
Tensile Strength	Yield 4	ASTM D638	33.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	34.0	Mpa
		Tensile Strength	Break 4	ASTM D638	27.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	28.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ASTM D152510	146	°C
	Vicat Softening Temperature	--	ISO 306/B50	103	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	107	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831	9.9E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	1.1E-4	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	110	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	71.0	°C

Injection	Test Result	Unit
Drying Time	2.0 到 4.0	hr
Suggested Shot Size	30 到 70	%
Rear Temperature	225 到 275	°C
Middle Temperature	240 到 280	°C
Front Temperature	250 到 290	°C
Nozzle Temperature	260 到 290	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	20 到 100	rpm
Vent Depth	0.038 到 0.051	mm
Drying Temperature	60 到 65	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	260 到 290	°C
Mold Temperature	30 到 50	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength	23°C	ASTM D4812	1400	J/m
	Unnotched Izod Impact Strength	-30°C 9	ISO 180/1U	无断裂
	Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C 9	ISO 180/1U	无断裂
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	6.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	12	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	80	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	无断裂
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	36.0	J

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.