PC/ABS CYCOLOY™ C1200HF WH9D409L SABIC INNOVATIVE NANSHA
47
- Unit Price:
- $2275 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance heat-resisting
- Application Areas:Electrical field Electronic field Automotive interior parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 260°C/5.0 kg | ASTM D1238 | 19 | g/10 min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | ASTM D638 | 2270 | Mpa | |
| Tensile Elongation | Yield | ASTM D638 | 5.0 | % |
| Break | ASTM D638 | 100 | % | |
| Flexural Modulus | 50.0 mm Span | ASTM D790 | 2340 | Mpa |
| Flexural Strength | Yield, 50.0 mm Span | ASTM D790 | 88.0 | Mpa |
| Tensile Strength | Yield | ASTM D638 | 57.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ISO 306/B50 | 130 | °C | |
| RTI | UL 746 | 105 | °C | |
| RTI Imp | UL 746 | 80.0 | °C | |
| RTI Elec | UL 746 | 105 | °C | |
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 129 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 112 | °C | |
| Coefficient of Linear Thermal Expansion (Flow) | -40 to 40°C | ASTM E831 | 7.2E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Comparative Tracking Index | UL 746 | PLC 2 | ||
| Hot-wire Ignition | UL 746 | PLC 3 | ||
| High Amp Arc Ignition | UL 746 | PLC 1 |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hopper Temperature | 60 到 80 | °C | ||
| Drying Time | 3.0 到 4.0 | hr | ||
| Suggested Shot Size | 30 到 80 | % | ||
| Rear Temperature | 250 到 290 | °C | ||
| Middle Temperature | 255 到 295 | °C | ||
| Front Temperature | 260 到 300 | °C | ||
| Nozzle Temperature | 275 到 300 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 40 到 70 | rpm | ||
| Vent Depth | 0.038 到 0.076 | mm | ||
| Drying Temperature | 100 到 110 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 275 到 300 | °C | ||
| Mold Temperature | 60 到 90 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | -30°C, Total Energy | ASTM D3763 | 54.0 | J |
| 23°C, Total Energy | ASTM D3763 | 54.0 | J |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 1.2 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.