Material Description
Technical Data Sheet
Material Description
- Material Properties:Oil resistant Fast forming cycle High mobility heat-resisting
- Application Areas:wheel Gear Connector bearing
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | Saturation, 23°C | ISO 62 | 8.0 到 9.0 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 2.5 到 3.1 | % | |
| Modeling Shrinkage | Across Flow | ISO 294-4 | 1.7 | % |
| 流量 | ISO 294-4 | 1.4 | % | |
| Apparent Density | 0.70 | g/cm³ | ||
| Viscosity number | 96% H2SO4 | ISO 307 | 150 | cm³/g |
| Melt Volume flow Rate | 275°C/5.0 kg | ISO 1133 | 100 | cm3/10min |
| Modeling Shrinkage | 0.85 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal Tensile Strain at Break | ISO 527-2/50 | 25 | % | |
| Tensile Creep Modulus | 1000 hr | ISO 899-1 | -- | Mpa |
| Tensile Stress | Yield | ISO 527-2/50 | 85.0 | Mpa |
| Tensile Strain | Yield | ISO 527-2/50 | 4.4 | % |
| Tensile Modulus | ISO 527-2 | 3000 | Mpa | |
| Flexural Modulus | ISO 178 | 2900 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 220 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 75.0 | °C | |
| Melting temperature | ISO 11357-3 | 260 | °C | |
| Specific Heat | 1700 | J/kg/°C | ||
| Thermal Conductivity | DIN 52612 | 0.33 | W/m/K | |
| Temperature Index | -- 5 | IEC 60216 | 147 | °C |
| -- 6 | IEC 60216 | 121 | °C | |
| Coefficient of Linear Thermal Expansion (Flow) | 23 to 80°C | ISO 11359-2 | 7.0E-5 到 1.0E-4 | cm/cm/°C |
| Maximum Service Temperature (short cycle operation) | 200 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation Factor? | 1 MHz | IEC 60250 | 0.025 | |
| Relative Permittivity | 1 MHz | IEC 60250 | 3.20 | |
| Comparative Tracking Index | Solution A | IEC 60112 | 500 | V |
| Surface Resistivity | IEC 60093 | -- | ohms | |
| Volume Resistivity | IEC 60093 | 1.0E+15 | ohms·cm |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Residence Time | < 10.0 | min | ||
| Screw Speed | < 18 | m/min | ||
| Hopper Temperature | 80 | °C | ||
| Drying Time | 4.0 | hr | ||
| Rear Temperature | 290 | °C | ||
| Middle Temperature | 290 | °C | ||
| Front Temperature | 290 | °C | ||
| Nozzle Temperature | 290 | °C | ||
| Drying Temperature | 80 | °C | ||
| Suggested Max Moisture | 0.15 | % | ||
| Processing (Melt) Temp | 280 到 300 | °C | ||
| Mold Temperature | 60 到 80 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 无断裂 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flammability level | 1.6 mm | IEC 60695-11-10, -20 | V-2 | |
| Polymer Abbreviation | PA66 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.