PC/ABS CYCOLOY™ CX7240-7M6D020 SABIC INNOVATIVE NANSHA

Unit Price:
$3875 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant High impact resistance High mobility
Application Areas:Electrical field Electronic field Electronic display Engine hood parts Aerospace Applications Nursing supplies Architectural application Outdoor applications Liquid handling Medical supplies Lighting fixtures
Color:--
Grade:Heat resistant grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	Saturation, 23°C	ISO 62	0.20	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.10	%
Melt Mass-Flow Rate	260°C/2.16 kg	ASTM D1238	18	g/10 min
Melt Volume flow Rate	260°C/2.16 kg	ISO 1133	15.0	cm3/10min
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.40 到 0.60	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	-- 5, 6	ISO 178	96.0	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	104	Mpa
Tensile Strength	Yield 3	ASTM D638	65.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	65.0	Mpa
		Tensile Strength	Break 3	ASTM D638	58.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	50.0	Mpa
Tensile Modulus	-- 2	ASTM D638	2600	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2600	Mpa
Tensile Elongation	Yield 3	ASTM D638	4.1	%
	Tensile Elongation	Yield	ISO 527-2/50	4.0	%
		Tensile Elongation	Break 3	ASTM D638	100	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	90	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	2500	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	2500	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ASTM D152511, ISO 306/B5011	110	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	113	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831, ISO 11359-2	7.5E-5	cm/cm/°C
	Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	7.5E-5	cm/cm/°C
	Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : -40°C	ISO 11359-2	7.5E-5	cm/cm/°C
Thermal Conductivity		ISO 8302	0.20	W/m/K
RTI		UL 746	90.0	°C
RTI Imp		UL 746	90.0	°C
RTI Elec		UL 746	90.0	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	100	°C
	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	89.0	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	99.0	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 10	ISO 75-2/Af	93.0	°C
Ball PressureTest	73 to 77°C	IEC 60695-10-2	通过

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	0.800 mm, in Oil	IEC 60243-1	35	KV/mm
	Dielectric Strength	1.60 mm, in Oil	IEC 60243-1	25	KV/mm
	Dielectric Strength	Dielectric Strength	3.20 mm, in Oil	IEC 60243-1	17	KV/mm
Comparative Tracking Index		UL 746	PLC 3
Hot-wire Ignition		UL 746	PLC 3
High Amp Arc Ignition		UL 746	PLC 0
Surface Resistivity		IEC 60093	> 1.0E+15	ohms
Volume Resistivity		IEC 60093	> 1.0E+15	ohms·cm

Injection	Test Result	Unit
Drying Temperature	80 到 90	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	250 到 300	°C
Mold Temperature	60 到 85	°C
Hopper Temperature	60 到 80	°C
Drying Time	2.0 到 4.0	hr
Rear Temperature	230 到 280	°C
Middle Temperature	240 到 290	°C
Front Temperature	250 到 300	°C
Nozzle Temperature	250 到 300	°C
Vent Depth	0.030 到 0.075	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	65.0	J

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	0.75 mm	IEC 60695-2-12	960	°C
Glow Wire Flammability Index	Glow Wire Flammability Index	0.75 mm 13	IEC 60695-2-12	960	°C
Oxygen Index		ISO 4589-2	34	%
Glow Wire Ignition Temperature	0.75 mm 13	IEC 60695-2-13	775	°C
	Glow Wire Ignition Temperature	1.0 mm	IEC 60695-2-13	825	°C
		Glow Wire Ignition Temperature	1.5 mm 13	IEC 60695-2-13	775	°C
			Glow Wire Ignition Temperature	3.0 mm	IEC 60695-2-13	800	°C
			Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0 mm 13	IEC 60695-2-13	775	°C
Flame Rating	0.60 mm	UL 94	V-1
	Flame Rating	0.75 mm	UL 94	V-0
		Flame Rating	1.5 mm	UL 94	5VB
		Flame Rating	Flame Rating	3.0 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.