Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 23°C/50% | ISO 62 | 0.3 | |
| Modeling Shrinkage(Across Flow) | / | ISO 294-4, 2577 | 2.2 | |
| Modeling Shrinkage (Across Flow) | / | ISO 294-4, 2577 | 1.9 | |
| 熔体体积流动速率(MVR)190℃/2.16 kg | / | ISO 1133 | 12 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | | 2800 | Mpa |
| Flexural Modulus | 23°C | ISO 178 | 2900 | Mpa |
| Flexural Strength | / | ISO 178 | 76 | Mpa |
| Tensile Elongation (Yield) | 50mm/mi | | 11 | % |
| Tensile Strength(Yield) | 50mm/mi | | 60 | Mpa |
| Tensile Elongation (Break) | 50mm/mi | | 30 | % |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength (-30°C) | | ISO 179/1eA | 6 | kJ/m² |
| Charpy Notched Impact Strength (23°C) | / | ISO 179/1eA | 7.5 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness(M-Scale) | | | 88 | |
| Ball Indentation Hardness | 30s | ISO 2039-1 | 137 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Coefficient of Linear Thermal Expansion(Flow) | Rate B/50 | | 90 | E-6/°C |
| Coefficient of Linear Thermal Expansion(Across Flow) | | | 90 | E-6/°C |
| Melt Temperature | 10°C/min | ISO 11357-1/-3 | 170 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.