Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 23°C,24hr | ISO62 | 0.50 | % |
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 0.80 | % |
| Moisture Absorption | Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % |
| Modeling Shrinkage | TD | ISO294-4 | 0.60 | % |
| Modeling Shrinkage | MD | ISO294-4 | 0.60 | % |
| Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 5.0 | g/10min |
| MediumDensity | | | 0.940 | g/cm³ |
| SpecificHeatCapacityofMelt | | | 2150 | J/kg/°C |
| ThermalConductivityofMelt | | | 0.15 | W/m/K |
| Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 5.00 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ISO527-2 | 24.0 | Mpa |
| Flexural Modulus | | ISO178 | 21.0 | Mpa |
| Tensile Stress | Break | ISO527-2 | 24.0 | Mpa |
| Tensile Stress | 10%Strain | ISO527-2 | 1.80 | Mpa |
| Tensile Stress | 50%Strain | ISO527-2 | 5.00 | Mpa |
| Tensile Strain | Break | ISO527-2 | >300 | % |
| Tensile Creep Modulus | 1000hr | ISO899-1 | 18.0 | Mpa |
| Tensile Creep Modulus | 1hr | ISO899-1 | 22.0 | Mpa |
| Nominal Tensile Strain at Break | | ISO527-2 | 900 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Brittleness Temperature | | ISO974 | -98.0 | °C |
| Glass Transition Temperature | | ISO11357-2 | -60.0 | °C |
| Effective Thermal Diffusivity | | | 5.44E-08 | m²/s |
| Melting Temperature | | ISO11357-3 | 177 | °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1.8E-04 | cm/cm/°C |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 2.1E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | | IEC60243-1 | 18 | KV/mm |
| Relative Permittivity | 100Hz | IEC60250 | 5.40 | |
| Relative Permittivity | 1MHz | IEC60250 | 5.30 | |
| Dissipation Factor? | 1MHz | IEC60250 | 0.015 | |
| Dissipation Factor? | 100Hz | IEC60250 | 7E-03 | |
| Surface Resistivity | | IEC60093 | 1E+14 | ohms |
| Volume Resistivity | | IEC60093 | 1E+13 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | Shore D,15sec | ISO868 | 26 | |
| Shore Hardness | Shore D | ISO868 | 30 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 3.0mm | UL94 | HB | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
| UL flame retardant rating | 3.0mm | IEC60695-11-10,-20 | HB | |
| Oxygen Index | | ISO4589-2 | 19 | % |
| FMVSS Flammability | | FMVSS302 | B | |
| Burning Rate | 1.00mm | ISO3795 | <100 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.