Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD | ISO294-4 | 1.4 | % |
| Modeling Shrinkage | TD | ISO294-4 | 1.5 | % |
| Moisture Absorption | 23°C,24hr | ISO62 | 35 | % |
| Moisture Absorption | Equilibrium,23°C,2.00mm,50%RH | ISO62 | 1.3 | % |
| MediumDensity | | | 1.02 | g/cm³ |
| Melt Volume flow Rate | 220°C/2.16kg | ISO1133 | 14.0 | cm3/10min |
| SpecificHeatCapacityofMelt3 | | | 2100 | J/kg/°C |
| ThermalConductivityofMelt3 | | | 0.16 | W/m/K |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Nominal Tensile Strain at Break | | ISO527-2 | 420 | % |
| Tensile Modulus | | ISO527-2 | 80.0 | Mpa |
| Flexural Modulus | | ISO178 | 80.0 | Mpa |
| Tensile Stress | Break | ISO527-2 | 20.0 | Mpa |
| Tensile Stress | 5.0%Strain | ISO527-2 | 3.40 | Mpa |
| Tensile Stress | 10%Strain | ISO527-2 | 5.40 | Mpa |
| Tensile Stress | 50%Strain | ISO527-2 | 9.50 | Mpa |
| Tensile Strain | Break | ISO527-2 | >300 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Effective Thermal Diffusivity | | | 5.44E-08 | m²/s |
| Melting Temperature | | ISO11357-3 | 200 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | Shore D | ISO868 | 40 | |
| Shore Hardness | Shore D,15sec | ISO868 | 38 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| FMVSS Flammability | | FMVSS302 | B | |
| Burning Rate | 1.00mm | ISO3795 | <100 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.