PA6 Durethan® BKV15 000000 DUS008 LANXESS WUXI

Unit Price:
$3375 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Glass fiber reinforced
Application Areas:Electronic and electrical Home appliance components Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD:280°C,3.00mm2	ISO2577	0.67	%
	Modeling Shrinkage	TD:120°C,2hr,3.00mm3	ISO294-4	0.21	%
		Modeling Shrinkage	MD:280°C,3.00mm2	ISO2577	0.34	%
		Modeling Shrinkage	Modeling Shrinkage	MD:120°C,2hr,3.00mm3	ISO2577	0.10	%
Moisture Absorption	Saturation,23°C	ISO62	7.8	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	2.6	%
Apparent Density		ISO60	0.70	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Break,23°C	ISO527-2/5	120	Mpa
Tensile Strain	Break,23°C	ISO527-2/5	3.0	%
Tensile Modulus	23°C	ASTMD638	6310	Mpa
Tensile Modulus	Tensile Modulus	23°C	ISO527-2/1	6300	Mpa
Tensile Elongation	Break,23°C	ASTMD638	3.0	%
Flexural Modulus	23°C	ASTMD790	5700	Mpa
Flexural Strength	23°C	ASTMD790	185	Mpa
Tensile Strength	Break,23°C	ASTMD638	117	Mpa
Flexural Stress	3.5%Strain	ISO178/A	--	Mpa
	Flexural Stress	23°C	ISO178	185	Mpa
	Flexural Stress	Flexural Stress	FlexuralStrainatFlexuralStrength5(23°C)		4.0	%
Flexural Modulus	23°C	ISO178/A	5700	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ISO306/B50	200	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B120	200	°C
Linear thermal expansion coefficient	MD：23to55°C	ISO11359-2	3E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：23to55°C	ISO11359-2	8E-05	cm/cm/°C
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	210	°C
	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	180	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	8.0MPa,Unannealed	ISO75-2/C	55.0	°C
Melting Temperature		ISO11357-3	218	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative Permittivity	23°C,100Hz	IEC60250	4.10
Relative Permittivity	Relative Permittivity	23°C,1MHz	IEC60250	3.70
Comparative Tracking Index	SolutionA	IEC60112	375	V
Surface Resistivity		IEC60093	1E+15	ohms
Volume Resistivity	23°C	IEC60093	1E+13	ohms·cm
Dielectric Strength	23°C,1.00mm	IEC60243-1	30	KV/mm
Dissipation Factor?	23°C,100Hz	IEC60250	8E-03
Dissipation Factor?	Dissipation Factor?	23°C,1MHz	IEC60250	0.018

Film	Test Condition	Test Method	Test Result	Unit
Film Puncture Energy	--6	ISO6603-2	1.50	J
Film Puncture Energy	Film Puncture Energy	--7	ISO6603-2	2.00	J
Film Puncture Force	--6	ISO6603-2	505	N
Film Puncture Force	Film Puncture Force	--7	ISO6603-2	560	N

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod impact strength	-30°C	ISO180/1U	20	kJ/m²
Notched Izod impact strength	Notched Izod impact strength	23°C	ISO180/1U	25	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	35	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	40	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness		ISO2039-1	190	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.6mm	UL94	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	UL94	HB
Glow Wire Flammability Index	2.0mm	IEC60695-2-12	650	°C
Oxygen Index		ISO4589-2	23	%
BurningBehavior10		ISO3795	passed

Supplementary information	Test Condition	Test Method	Test Result	Unit
ISO Shortname		ISO1874	PA6/66,GHR,14-060,GF15

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.