Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD:2.00mm | ISO294-4 | 2.0 | % |
| Modeling Shrinkage | MD:2.00mm | ISO294-4 | 2.0 | % |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.50 | % |
| Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 8.00 | cm3/10min |
| Melt Mass-Flow Rate | | ASTMD1238 | 9.0 | g/10min |
| Melt Mass-Flow Rate | | ISO1133 | 9.0 | g/10min |
| Density / Specific Gravity | | ISO1183 | 1.41 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Nominal Tensile Strain at Break | | ISO527-2 | 35 | % |
| Flexural Stress | | ISO178 | 87.0 | Mpa |
| Coefficient of Friction | Dynamic2 | JISK7218 | 0.37 | |
| Coefficient of Friction | Steel - Dynamic3 | JISK7218 | 0.46 | |
| Coefficient of Friction | Steel - Dynamic4 | JISK7218 | 0.40 | |
| Specific Wear Rate | 0.98MPa,0.30m/sec5 | JISK7218 | <1.0 | 10^-8mm³/N·m |
| Specific Wear Rate | 0.49MPa,0.30m/sec5 | JISK7218 | <1.0 | 10^-8mm³/N·m |
| Specific Wear Rate | 0.98MPa,0.30m/sec6 | JISK7218 | 30 | 10^-8mm³/N·m |
| Specific Wear Rate | 0.49MPa,0.30m/sec6 | JISK7218 | 65 | 10^-8mm³/N·m |
| Specific Wear Rate | 0.060MPa,0.15m/sec7 | JISK7218 | 3500 | 10^-8mm³/N·m |
| Specific Wear Rate | 0.060MPa,0.15m/sec8 | JISK7218 | 6500 | 10^-8mm³/N·m |
| Tensile Stress | | ISO527-2 | 62.0 | Mpa |
| Tensile Modulus | | ISO527-2 | 2700 | Mpa |
| Flexural Modulus | | ISO178 | 2500 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 95.0 | °C |
| Linear thermal expansion coefficient | MD：23to55°C | 内部方法 | 1.2E-04 | cm/cm/°C |
| Linear thermal expansion coefficient | TD：23to55°C | 内部方法 | 1.2E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | IEC60093 | 1E+16 | ohms |
| Volume Resistivity | | IEC60093 | 1E+14 | ohms·cm |
| Dielectric Strength | 3.00mm | IEC60243-1 | 19 | KV/mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 6.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M-Scale | ISO2039-2 | 80 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | HB | |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| Color Number | | | CF2001/CD3068 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.