Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:3.00mm | ASTMD955 | 1.8到2.2 | % |
Moisture Absorption | Equilibrium,23°C,69%RH | ASTMD570 | 0.22 | % |
Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 9.0 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Compressive Strength | 1%Strain | ASTMD695 | 31.4 | Mpa |
Compressive Strength | 10%Strain | ASTMD695 | 108 | Mpa |
Tensile Elongation | Break | ASTMD638 | 60 | % |
Flexural Modulus | | ASTMD790 | 2550 | Mpa |
Flexural Strength | | ASTMD790 | 93.2 | Mpa |
Tensile Strength | Yield | ASTMD638 | 60.8 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ASTMD1525 | 162 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 158 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 110 | °C |
Linear thermal expansion coefficient | MD | ASTMD696 | 8.5E-05 | cm/cm/°C |
Melting temperature | | DSC | 165 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | 2.00mm | ASTMD149 | 24 | KV/mm |
Dielectric Constant | 50Hz | IEC60250 | 3.80 | |
Dielectric Constant | 1kHz | IEC60250 | 3.80 | |
Dielectric Constant | 1MHz | IEC60250 | 3.80 | |
Surface Resistivity | | ASTMD257 | 1E+16 | ohms |
Volume Resistivity | 23°C | ASTMD257 | 1E+14 | ohms·cm |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M-Scale | ASTMD785 | 80 | |
Rockwell Hardness | R-Scale | ASTMD785 | 115 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.