| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D955 | 1.22 | % |
| Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 10 | g/10min |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Taber wear | CS-17轮 | ASTM D-1044 | 9 | mg/1000rev |
| Taber wear | H 18轮 | ASTM D-1044 | 116 | mg/1000rev |
| Melt index | | ASTM D-1238 | 10 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation?(Break) | | ASTM D412/ISO 527 | 31 | % |
| Rockwell Hardness | | ASTM D785 | 55 | |
| Flexural Modulus | | ASTM D790/ISO 178 | 193 | kg/cm²(MPa)[Lb/in²] |
| Tensile Strength | 5%伸长 | ASTM D-638 | 6.0 | Mpa |
| Tensile Strength | 10%伸长 | ASTM D-638 | 10.5 | Mpa |
| Notched Izod Impact Strength | 23℃ | ASTM D-256 | 不破裂 | J/m |
| Tensile Elongation (Break) | | ASTM D-648 | 375 | % |
| Tensile Modulus | 23℃ | ASTM D-790 | 193 | Mpa |
| Tensile Strength (Break) | | ASTM D-638 | 31 | Mpa |
| Durometer Hardness | | ASTM D-2240 | 55 | |
| Tearing Strength | | ASTM D-1004 | 123 | kN/m |
| Tensile Elongation?(Break) | | ASTM D412/ISO 527 | 375 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melting Temperature | | ASTM D-3418 | 215 | °C |
| Melting Temperature | | | 215 | ℃（℉） |
| Vicat Softening Temperature | | ASTM D1525/ISO R306 | 196 | ℃（℉） |
| Vicat Softening Temperature | | ASTM D-1525 | 196 | °C |
| Thermal distortion temperature | @0.18Mpa | ASTM D-648 | 51 | °C |
| Thermal distortion temperature | @0.5Mpa | ASTM D-648 | 111 | °C |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption (24hr) | | ASTM D-570 | 1.5 | % |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Ross Flex | | ASTM D-1052 | >8×10 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.