TPEE Hytrel® 8238 DUPONT USA

Unit Price:
$8350 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Dongguan Kenai New Material Co., Ltd.

+86 132****36

kntp********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	ISO294-4	1.6	%
Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	1.6	%
Moisture Absorption	23°C,24hr	ISO62	0.30	%
	Moisture Absorption	Saturation,23°C,2.00mm	ISO62	0.60	%
	Moisture Absorption	Moisture Absorption	Equilibrium,23°C,2.00mm,50%RH	ISO62	0.20	%
MediumDensity			1.13	g/cm³
SpecificHeatCapacityofMelt			2150	J/kg/°C
ThermalConductivityofMelt			0.15	W/m/K
Melt Mass-Flow Rate	240°C/2.16kg	ISO1133	13	g/10min
Melt Volume flow Rate	240°C/2.16kg	ISO1133	11.5	cm3/10min
Density / Specific Gravity		ISO1183	1.28	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Nominal Tensile Strain at Break		ISO527-2	340	%
Tensile Stress	Yield	ISO527-2	38.0	Mpa
	Tensile Stress	Break	ISO527-2	46.0	Mpa
		Tensile Stress	10%Strain	ISO527-2	34.0	Mpa
			Tensile Stress	50%Strain	ISO527-2	28.0	Mpa
			Tensile Stress	Tensile Stress	100%Strain	ISO527-2	26.0	Mpa
Tensile Strain	Yield	ISO527-2	19	%
Tensile Strain	Tensile Strain	Break	ISO527-2	>300	%
Tensile Modulus		ISO527-2	1200	Mpa
Flexural Modulus		ISO178	1150	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	105	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	45.0	°C
Brittleness Temperature		ISO974	-84.0	°C
Vicat Softening Temperature	--	ISO306/A50	213	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B50	150	°C
Linear thermal expansion coefficient	MD：--	ISO11359-2	1.5E-04	cm/cm/°C
	Linear thermal expansion coefficient	MD：-40to23°C	ISO11359-2	9E-05	cm/cm/°C
		Linear thermal expansion coefficient	TD：--	ISO11359-2	1.4E-04	cm/cm/°C
			Linear thermal expansion coefficient	TD：-40to23°C	ISO11359-2	1E-04	cm/cm/°C
			Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：EffectiveThermalDiffusivity	ISO11359-2	5.44E-08	m²/s
Glass Transition Temperature		ISO11357-2	50.0	°C
Melting Temperature		ISO11357-3	221	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength		IEC60243-1	21	KV/mm
Relative Permittivity	100Hz	IEC60250	4.00
Relative Permittivity	Relative Permittivity	1MHz	IEC60250	3.70
Comparative Tracking Index		IEC60112	600	V
Surface Resistivity		IEC60093	>1.0E+15	ohms
Volume Resistivity		IEC60093	>1.0E+15	ohms·cm
Dissipation Factor?	100Hz	IEC60250	0.010
Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	0.018

Elastomers Properties	Test Condition	Test Method	Test Result	Unit
Tearing Strength	Across Flow	ISO34-1	210	kN/m
Tearing Strength	Tearing Strength	流量	ISO34-1	230	kN/m

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-40°C	ISO179/1eA	5.0	kJ/m²
	Charpy Notched Impact Strength	-30°C	ISO179/1eA	5.0	kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	15	kJ/m²
Notched Izod Impact Strength	-40°C	ISO180/1A	5.5	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	11	kJ/m²
Tensile Impact Strength	23°C	ISO8256/1	57.0	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Shore Hardness	Shore D	ISO868	76
Shore Hardness	Shore Hardness	Shore D,15sec	ISO868	70

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.9mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
		UL flame retardant rating	0.9mm	IEC60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC60695-11-10,-20	HB
Oxygen Index		ISO4589-2	22	%
FMVSS Flammability		FMVSS302	SE

Supplementary information	Test Condition	Test Method	Test Result	Unit
EmissionofOrganicCompounds		VDA277	550	µgC/g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Port of Loading	Unit Price
China Main Port	7432 USD/MT