PEI ULTEM™ 1000 SABIC INNOVATIVE US
184
- Unit Price:
- $22884 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Flame retardant enhance
- Application Areas:Electrical field Electronic field Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.25 | % |
| Equilibrium,23°C | ASTMD570 | 1.3 | % | |
| Melt mass flow rate | 337°C/6.6kg | ASTMD1238 | 9.0 | g/10min |
| Density/specific gravity | ASTMD792 | 1.27 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Strength4 | Yield,100mmSpan | ASTMD790 | 165 | Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | ASTMD1044 | 10.0 | mg |
| Poisson's ratio | ASTMD638 | 0.36 | ||
| Elongation rate 3 | Yield | ASTMD638 | 7.0 | % |
| Tensile modulus 2 | ASTMD638 | 3590 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 110 | Mpa |
| Bending modulus 4 | 100mmSpan | ASTMD790 | 3520 | Mpa |
| Elongation rate 4 | Break | ASTMD638 | 60 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| thermal conductivity | ASTMC177 | 0.22 | W/m/K | |
| RTIElec | UL746 | 170 | °C | |
| Evolution Calendar intelligent importer | UL746 | 170 | °C | |
| RTIStr | UL746 | 170 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 210 | °C |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 201 | °C | |
| Linear coefficient of thermal expansion | MD：-20to150°C | ASTME831 | 5.6E-05 | cm/cm/°C |
| TD：-20to150°C | ASTME831 | 5.4E-05 | cm/cm/°C | |
| Vicat softening temperature | ASTMD15255 | 219 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 1.60mm,inAir | ASTMD149 | 33 | KV/mm |
| 1.60mm,in Oil | ASTMD149 | 28 | KV/mm | |
| 3.20mm,in Oil | ASTMD149 | 20 | KV/mm | |
| Dielectric constant | 100Hz | ASTMD150 | 3.15 | |
| 1kHz | ASTMD150 | 3.15 | ||
| Volume resistivity | ASTMD257 | 1E+17 | ohms·cm | |
| Dissipation factor | 100Hz | ASTMD150 | 1.5E-03 | |
| 1kHz | ASTMD150 | 1.2E-03 | ||
| 2.45GHz | ASTMD150 | 2.5E-03 | ||
| Arc resistance 6 | ASTMD495 | PLC5 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC4 | |
| Hot wire ignition | HWI | UL746 | PLC1 | |
| High arc combustion index | HAI | UL746 | PLC3 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC2 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Falling hammer impact | 23°C | ASTMD3029 | 36.6 | J |
| ReverseNotchIzodImpact | 3.20mm | ASTMD256 | 1300 | J/m |
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 53 | J/m |
| 23°C | ASTMD4812 | 1300 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ASTMD785 | 109 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ASTMD2863 | 47 | % | |
| UL flame retardant rating | 0.40mm | UL94 | V-2 | |
| 0.75mm | UL94 | V-0 | ||
| 3.0mm | UL94 | 5VA | ||
| NBSSmokeDensity-Flaming,Ds,4min | ASTME662 | 0.700 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.