Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 23℃,24hr | % | 0,15到0,53 | |
-- | | | 1,21到1,66 | |
23℃ | | g/cm³ | 1,37到1,72 | |
23℃ | | % | 3,0E-3到1,1 | |
Flow:23℃ | | mm/mm | 25.4E-3到134.6E-3 | |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
23℃ | | MPa | 168.97到246.9 | |
23℃ | | MPa | 3296.55到0.02,0.04E0.05 | |
23℃ | | MPa | 6420.69到0.01,0.05E0.05 | |
23℃ | | MPa | 3331.03到0.01,0.01E0.05 | |
23℃ | | MPa | 2572.41到0.01,0.02E0.05 | |
23℃ | | MPa | 157.93到348.97 | |
23℃ | | MPa | 119.31到235.17 | |
23℃ | | MPa | 86.21到417.24 | |
Break,23℃ | | % | 1,7到2,7 | |
Break,23℃ | | MPa | 26.0到260.0 | |
Break,23℃ | | MPa | 56.0到260.0 | |
Break,23℃ | | % | 2,0到4,6 | |
Yield,23℃ | | MPa | 27.03到260.0 | |
Yield,23℃ | | % | 1,5到5,0 | |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | MD | mm/mm/°C | 30.5E-5到50.8E-5 | |
Melting temperature | | °C | 220到265 | |
0.45MPa, Unannealed | | °C | 253到262 | |
0.45MPa, Unannealed | | °C | 137到223 | |
1.8MPa, Unannealed | | °C | 139到288 | |
1.8MPa, Unannealed | | °C | 223到270 | |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | 23℃ | V/mil | 490到610 | |
Comparative Tracking Index | | V | 593到600 | |
Surface Resistivity | | ohms | 1,0E+12到1,0E+14 | |
Volume Resistivity | 23℃ | ohms·cm | 1,0E+4到1,0E+16 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23℃ | kJ/m² | 7.892到21.357 | |
Unnotched Izod Impact Strength | 23℃ | J/m | 0.085到0.462 | |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | 23℃ | | 122到125 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.