Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | | DENKA Method | 0.2-0.4 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | 23℃ | ISO 2039-2(JIS K7202) | 83 | M |
| Flexural Strength | 2mm/min | ISO 178(JIS K7171) | 120 | Mpa |
| Bending elasticity | 2mm/min | ISO 178(JIS K7171) | 3560 | Mpa |
| Notched Izod Impact Strength | Notched,23℃ | ISO 179(JIS K7111) | 1.5 | KJ/m |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 1.80MPa | ISO 75-1,-2(JIS K7191-1,-2) | 84 | °C |
| Vicat Softening Temperature | 50N | ISO 306(JIS K7206) | 84 | °C |
| Flammability | | UL 94(UL File No.E49895) | HB | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Transmittance | 2mmt | ISO 13468-1(JIS K7361) | 90.2 | % |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 200℃,49N | ISO 1133(JIS K7210) | 3.0 | g/10min |
| Density | 23℃ | ISO 1183(JIS K7112) | 1067 | kg/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.