Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD：3.20mm	内部方法	0.40to0.80	%
Moisture Absorption	饱和,23°C	ISO62	0.40	%
Moisture Absorption	Moisture Absorption	平衡,23°C,50%RH	ISO62	0.15	%
Melt Mass-Flow Rate	300°C/1.2kg	ASTMD1238	16	g/10min
Melt Volume flow Rate	300°C/1.2kg	ISO1133	15.1	cm3/10min
Density		ASTMD792	1.19	g/cm³
Density	Density		ISO1183	1.19	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength	断裂	ASTMD638	59.0	Mpa
Tensile Strength	Tensile Strength	屈服	ASTMD638	58.0	Mpa
Tensile Stress	断裂	ISO527-2/50	57.0	Mpa
Tensile Stress	Tensile Stress	屈服	ISO527-2/50	56.0	Mpa
Tensile Strain	断裂	ISO527-2/50	110	%
Tensile Strain	Tensile Strain	屈服	ISO527-2/50	6.0	%
Tensile Modulus		ASTMD638	2100	Mpa
Tensile Modulus	Tensile Modulus		ISO527-2/1	2000	Mpa
Tensile Elongation	屈服	ASTMD638	6.0	%
Tensile Elongation	Tensile Elongation	断裂	ASTMD638	120	%
Flexural Modulus	50.0mm跨距	ASTMD790	2400	Mpa
Flexural Modulus	Flexural Modulus		ISO178	2100	Mpa
Flexural Strength		ISO178	87.0	Mpa
Flexural Strength	Flexural Strength	屈服,50.0mm跨距	ASTMD790	92.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8MPa,Unannealed,64.0mmSpan	ISO75-2/Af	118	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,未退火,3.20mm	ASTMD648	123	°C
RTIElec		UL746	125	°C
Evolution Calendar intelligent importer		UL746	115	°C
RTIStr		UL746	120	°C
Linear thermal expansion coefficient	MD：-40到40°C	ASTME831	6.1E-05	cm/cm/°C
	Linear thermal expansion coefficient	MD：-40到40°C	ISO11359-2	6.1E-05	cm/cm/°C
		Linear thermal expansion coefficient	TD：-40到40°C	ASTME831	6.2E-05	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：-40到40°C	ISO11359-2	6.2E-05	cm/cm/°C
Vicat Softening Temperature		ASTMD152510	140	°C
	Vicat Softening Temperature	--	ISO306/B50	139	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B120	141	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	67.0	J
Charpy Notched Impact Strength	-30°C	ISO179/1eA	35	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	70	kJ/m²
Notched Izod Impact Strength	-30°C	ASTMD256	660	J/m
	Notched Izod Impact Strength	23°C	ASTMD256	790	J/m
		Notched Izod Impact Strength	-30°C	ISO180/1A	30	kJ/m²
		Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	65	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	1.6mm	IEC60695-2-12	960	°C
Glow Wire Ignition Temperature	1.5mm	IEC60695-2-13	825	°C
Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0mm	IEC60695-2-13	825	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.