PBT VALOX™ ENH4560 BK1066 SABIC INNOVATIVE SHANGHAI
78
- Unit Price:
- $7196 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Bromine free Chlorine free
- Application Areas:Electronic display Automotive External Parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 265°C/5.0kg | ASTMD1238 | 23 | g/10min |
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 16.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fracture bending strain 11 | ISO178 | 2.0 | % | |
| --1 | ASTMD638 | 11000 | Mpa | |
| Surrender 2 | ASTMD638 | 110 | Mpa | |
| yield | ISO527-2/5 | 105 | Mpa | |
| Fracture 3 | ASTMD638 | 110 | Mpa | |
| crack | ISO527-2/5 | 105 | Mpa | |
| Surrender 4 | ASTMD638 | 2.0 | % | |
| yield | ISO527-2/5 | 2.0 | % | |
| Fracture 5 | ASTMD638 | 2.0 | % | |
| crack | ISO527-2/5 | 2.0 | % | |
| 50.0mm span 6 | ASTMD790 | 9000 | Mpa | |
| --7 | ISO178 | 10000 | Mpa | |
| --8 | ISO178 | 170 | Mpa | |
| Yield, 50.0mm span 9 | ASTMD790 | 150 | Mpa | |
| Fracture, 50.0mm span of 10 | ASTMD790 | 150 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| -- | ASTMD152520 | 217 | °C | |
| ISO306/A50 | 220 | °C | ||
| ISO306/B50 | 206 | °C | ||
| ISO306/B120 | 205 | °C | ||
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD:-40to40°C | ISO11359-2 | 2E-05 | cm/cm/°C |
| MD:23to150°C | ISO11359-2 | 2.5E-05 | cm/cm/°C | |
| TD:-40to40°C | ISO11359-2 | 6.2E-05 | cm/cm/°C | |
| TD:23to150°C | ISO11359-2 | 1.5E-04 | cm/cm/°C | |
| RTIElec | UL746 | 140 | °C | |
| Evolution Calendar intelligent importer | UL746 | 125 | °C | |
| RTI | UL746 | 140 | °C | |
| 0.45MPa, unannealed, 3.20mm | ASTMD648 | 223 | °C | |
| 0.45MPa, unannealed, 64.0mm span 17 | ISO75-2/Bf | 225224 | °C | |
| 1.8MPa, unannealed, 3.20mm | ASTMD648 | 210 | °C | |
| 1.8MPa, unannealed, 64.0mm span 18 | ISO75-2/Af | 210 | °C | |
| -- | ASTMD152519 | 207 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | ASTMD257,IEC60093 | 1E+14 | ohms·cm | |
| 0.800mm,inOil | ASTMD149 | 32 | KV/mm | |
| 1.60mm,inOil | ASTMD149 | 22 | KV/mm | |
| 3.20mm, inoil | ASTMD149 | 18 | KV/mm | |
| 0.800mm, in oil | IEC60243-1 | 32 | KV/mm | |
| 1.60mm, in oil | IEC60243-1 | 22 | KV/mm | |
| 3.20mm, in oil | IEC60243-1 | 18 | KV/mm | |
| Dielectric constant | 1MHz | ASTMD150,IEC60250 | 3.80 | |
| Dissipation factor | 1MHz | ASTMD150,IEC60250 | 0.14 | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC0 | |
| Leakage Trace Index | IEC60112 | 600 | V | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| Hot wire ignition | HWI | UL746 | PLC0 |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 260°C,1500sec^-1 | ISO11443 | 110 | Pa·s |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 23°C14 | ISO180/1A | 9.0 | kJ/m² | |
| -30°C | ASTMD4812 | 500 | J/m | |
| 23°C | ASTMD4812 | 500 | J/m | |
| -30°C15 | ISO180/1U | 37 | kJ/m² | |
| 23°C16 | ISO180/1U | 37 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/2U | 35 | kJ/m² |
| 23°C | ISO179/2U | 40 | kJ/m² | |
| -30°C | ASTMD256 | 75 | J/m | |
| 0°C | ASTMD256 | 75 | J/m | |
| 23°C | ASTMD256 | 75 | J/m | |
| -30°C12 | ISO180/1A | 9.0 | kJ/m² | |
| 0°C13 | ISO180/1A | 9.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale | ISO2039-2 | 120 | |
| Ball pressure hardness | H358/30 | ISO2039-1 | 142 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.800mm | UL94 | V-0 | |
| 3.00mm | UL94 | 5VB | ||
| Burning wire flammability index | 2.00mm | IEC60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.00mm | IEC60695-2-13 | 750 | °C |
| 2.00mm | IEC60695-2-13 | 750 | °C | |
| 3.00mm | IEC60695-2-13 | 800 | °C |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Filling material | ASTMD229 | 30 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.