Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Across Flow | ISO 2577 | 0.20 到 0.30 | % |
Modeling Shrinkage | 流量 | ISO 2577 | 0.20 到 0.30 | % |
Moisture Absorption | Saturation, 23°C | ISO 62 | 0.50 | % |
Moisture Absorption | Equilibrium, 23°C, 50% RH | ISO 62 | 0.20 | % |
Melt Volume flow Rate | 260°C/5.0 kg | ISO 1133 | 24.0 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | 23°C | ISO 527-2/1 | 5400 | Mpa |
Tensile Stress | Yield, 23°C | ISO 527-2/50 | 62.0 | Mpa |
Tensile Stress | Break, 23°C | ISO 527-2/50 | 48.0 | Mpa |
Tensile Strain | Yield, 23°C | ISO 527-2/50 | 3.2 | % |
Tensile Strain | Break, 23°C | ISO 527-2/50 | 6.0 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 96.0 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 88.0 | °C |
Vicat Softening Temperature | -- | ISO 306/B50 | 99.0 | °C |
Vicat Softening Temperature | -- | ISO 306/B120 | 102 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC 60093 | 1.0E+16 | ohms |
Volume Resistivity | 23°C | IEC 60093 | 1.0E+17 | ohms·cm |
Fill Analysis | Test Condition | Test Method | Test Result | Unit |
---|
Melt Viscosity | 260°C | ISO 11443-A | 220 | Pa·s |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod impact strength | 23°C | ISO 180 | 52 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Glow Wire Flammability Index | 1.0 mm | IEC 60695-2-12 | 850 | °C |
Flame Rating | 1.2 mm | UL 94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.