Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD2.0mm | ISO294-4 | 0.60 | % |
Modeling Shrinkage | TD2.0mm | ISO294-4 | 0.60 | % |
Moisture Absorption | (23°C,24hr) | ISO62 | 0.50 | % |
Moisture Absorption | (23°C,50RH) | ISO62 | 0.20 | % |
Melt Mass-Flow Rate | 240℃/5.0Kg | ISO1133 | 19 | cm3/10min |
Density / Specific Gravity | | ISO1183 | 1.18 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | 23°C | ISO180/1A | 30 | kJ/m² |
Tensile Elongation?(Break) | 23°C | ISO527-2 | >50 | % |
Tensile Modulus | 23°C | ISO527-2 | 2700 | Mpa |
Tensile Strength | 23°C | ISO527-2 | 60 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPaUnannealed | ISO75-2/Bf | 92 | °C |
Deflection Temperature Under Load? | 1.80MPaAnnealed | ISO75-2/Af | 84 | °C |
Vicat Softening Temperature | | ISO306/B50 | 97 | °C |
Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 7.6E-05 | cm/cm/°C |
Coefficient of Linear Thermal Expansion | TD | ISO11359-2 | 8E-05 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Insulation strength | | IEC60243-1 | 35 | KV/mm |
Volume Resistivity | | IEC60093 | 1E+16 | Ω.cm |
Surface resistance | | IEC60093 | 1E+16 | Ω.cm |
Dielectric Constant | 23°C | IEC60250 | 3.10 | 1MHz |
Dissipation Factor? | 23°C | IEC60250 | 6E-03 | 1MHz |
Dissipation Factor? | 相对漏电起痕指数 | IEC60112 | 300 | V |
Flame Rating | Test Condition | Test Method | Test Result | Unit |
---|
Fire rating | | UL-94 | 0.75mm | |
Fire rating | | UL-94 | 0.90mm | V-0 |
Fire rating | | UL-94 | 1.00mm | V-0 |
Fire rating | | UL-94 | 1.50mm | V-0 |
Fire rating | | UL-94 | 1.80mm | V-0,5VB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.