PBT VALOX™ ENH4560 BK1066 SABIC INNOVATIVE NANSHA

Unit Price:
$6587 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant Bromine free Chlorine free
Application Areas:Electronic display Automotive External Parts
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	265°C/5.0kg	ASTMD1238	23	g/10min
Melt Volume flow Rate	250°C/5.0kg	ISO1133	16.0	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
50.0mm Span		ASTMD790	9000	Mpa
--7		ISO178	10000	Mpa
--8		ISO178	170	Mpa
--1		ASTMD638	11000	Mpa
Yield		ASTMD638	2.0	%
Break		ASTMD638	2.0	%
yield		ISO527-2/5	105	Mpa
yield	yield		ISO527-2/5	2.0	%
fracture		ISO527-2/5	105	Mpa
fracture	fracture		ISO527-2/5	2.0	%
Yield		ASTMD638	110	Mpa
Break		ASTMD638	110	Mpa
Yield,50.0mm Span		ASTMD790	150	Mpa
Break,50.0mm Span		ASTMD790	150	Mpa
Flexural Strain (Break)		ISO178	2.0	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
0.45MPa, Unannealed,3.20mm Span		ISO75-2/Bf	225224	°C
1.8MPa, Unannealed,64.0mm Span		ISO75-2/Af	210	°C
1.8MPa, Unannealed,3.20mm		ASTMD648	210	°C
RTI		UL746	140	°C
0.45MPa, Unannealed,3.20mm		ASTMD648	223	°C
--		ASTMD152519	207	°C
	--		ASTMD152520	217	°C
		--		ISO306/A50	220	°C
			--		ISO306/B50	206	°C
			--	--		ISO306/B120	205	°C
Ball PressureTest	125°C	IEC60695-10-2	Pass
RTIElec		UL746	140	°C
Evolution Calendar intelligent importer		UL746	125	°C
Linear thermal expansion coefficient	MD:-40to40°C	ISO11359-2	2E-05	cm/cm/°C
	Linear thermal expansion coefficient	MD:23to150°C	ISO11359-2	2.5E-05	cm/cm/°C
		Linear thermal expansion coefficient	TD:-40to40°C	ISO11359-2	6.2E-05	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD:23to150°C	ISO11359-2	1.5E-04	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		IEC60093	>1.0E+15	ohms
Dielectric Constant	1MHz	ASTMD150,IEC60250	3.80
Volume Resistivity		ASTMD257,IEC60093	1E+14	ohms·cm
Dissipation Factor?	1MHz	ASTMD150,IEC60250	0.14
Comparative Tracking Index		IEC60112	600	V
Comparative Tracking Index	CTI	UL746	PLC0
Hot-wire Ignition	HWI	UL746	PLC0
High Amp Arc Ignition	HAI	UL746	PLC0
1.60mm,inOil		ASTMD149	22	KV/mm
3.20mm,inOil		ASTMD149	18	KV/mm
0.800mm, in oil		IEC60243-1	32	KV/mm
1.60mm,in Oil		IEC60243-1	22	KV/mm
3.20mm,in Oil		IEC60243-1	18	KV/mm
0.800mm,inOil		ASTMD149	32	KV/mm

Fill Analysis	Test Condition	Test Method	Test Result	Unit
Melt Viscosity	260°C,1500sec^-1	ISO11443	110	Pa·s

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO179/2U	35	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/2U	40	kJ/m²
0°C13		ISO180/1A	9.0	kJ/m²
23°C		ASTMD256	75	J/m
23°C	23°C		ASTMD4812	500	J/m
-30°C12		ISO180/1A	9.0	kJ/m²
-30°C		ASTMD256	75	J/m
-30°C	-30°C		ASTMD4812	500	J/m
0°C		ASTMD256	75	J/m
-30°C15		ISO180/1U	37	kJ/m²
23°C14		ISO180/1A	9.0	kJ/m²
23°C16		ISO180/1U	37	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Sale	ISO2039-2	120
Ball Indentation Hardness	H358/30	ISO2039-1	142	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.800mm	UL94	V-0
UL flame retardant rating	UL flame retardant rating	3.00mm	UL94	5VB
Glow Wire Flammability Index	2.00mm	IEC60695-2-12	960	°C
Glow Wire Ignition Temperature	2.00mm	IEC60695-2-13	750	°C
	Glow Wire Ignition Temperature	3.00mm	IEC60695-2-13	800	°C
	Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	1.00mm	IEC60695-2-13	750	°C

Supplementary information	Test Condition	Test Method	Test Result	Unit
Filler Content		ASTMD229	30	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.