PC Makrolon® 2805 021139 COVESTRO THAILAND
10
- Unit Price:
- $3601 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume flow Rate | 250℃；2.16kg | cm3/(10分钟) | ISO 1133 | -- |
| 300℃；1.2kg | cm3/(10分钟) | ISO 1133 | 9.5 | |
| Modeling Shrinkage (Flow) | 60*60*2；500bar | % | ISO 294-4 | 0.65 |
| Modeling Shrinkage (Across Flow) | 60*60*2；500bar | % | ISO 294-4 | 0.7 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress (Yield) | 23℃/50%r.h 50毫米/分钟 | % | ISO 527-1-2 | 6.1 |
| Tensile Modulus | 23℃/50%r.h 1毫米/分钟 | MPa | ISO 527-1-2 | 2400 |
| Notched Impact Strength | 23℃/50%r.h ；3.2毫米 | kJ/m² | 参照ISO 180/1eA | 85P(C) |
| Tensile Creep Modulus | 23℃/50%r.h 1hr | MPa | ISO 899-1 | 2200 |
| 23℃/50%r.h 1000hr | MPa | ISO 899-1 | 1900 | |
| Fracture strain | 23℃/50%r.h 5毫米/分钟 | % | ISO 527-1-2 | -- |
| Tensile Stress (Yield) | 23℃/50%r.h 50毫米/分钟 | MPa | ISO 527-1-2 | 66 |
| Elongation at break | 23℃/50%r.h 50毫米/分钟 | % | ISO 527-1-2 | ＞50 |
| Flexural Modulus | 23℃/50%r.h 2毫米/分钟 | MPa | ISO 179 | 2400 |
| Tensile Stress(Break) | 23℃/50%r.h 5毫米/分钟 | MPa | ISO 527-1-2 | -- |
| Charpy Notched Impact Strength | 23℃/50%r.h | kJ/m² | ISO 179/1eU | N |
| Charpy Notched Impact Strength | 23℃/50%r.h ；3毫米 | kJ/m² | 参照ISO 179/1eA | 75P(C) |
| Tensile Strength (Break) | 23℃/50%r.h | N | ISO 6603-2 | 5400 |
| 破坏能 | 23℃/50%r.h | J | ISO 6603-2 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Coefficient of Linear Thermal Expansion (Flow) | 23-55℃ | 10-4/K | ISO 11359-1-2 | 0.65 |
| Coefficient of Linear Thermal Expansion (Across Flow) | 23-55℃ | 10-4/K | ISO 11359-1-2 | 0.65 |
| Flame Rating | 1.5毫米 | 级 | UL 94 | V-2 |
| 厚度 | 级 | UL 94 | HB(2.5) | |
| Flame Rating | 3.0毫米 | 级 | UL 94 | |
| Glow Wire Flammability Index | 1.5毫米 | ℃ | IEC 60695-2-12 | 850 |
| 1.0毫米 | ℃ | IEC 60695-2-12 | 930 | |
| Glow Wire Ignition Temperature | 1.5毫米 | ℃ | IEC 60695-2-13 | 875 |
| 3.0毫米 | ℃ | IEC 60695-2-13 | 875 | |
| Deflection Temperature Under Load? | 1.80MPa | ℃ | ISO 75-1-2 | |
| 0.45MPa | ℃ | ISO 75-1-2 | ||
| Glass Transition Temperature | 10℃/毫米 | ℃ | ISO 11357-1-2 | 145 |
| Vicat Softening Temperature | 50N；50℃/hr | ℃ | ISO 306 | 145 |
| Oxygen Index | A溶液 | % | ISO 4589-2 | 27 |
| other | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density / Specific Gravity | -- | kg/m2 | ISO 1183 | 1200 |
| Moisture Absorption | 在23℃水中 | % | ISO 62 | 0.30 |
| Moisture Absorption | 23℃：50%rh | % | ISO 62 | 0.12 |
| Other Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Index of Refraction | 过程A | -- | ISO 489 | 1.586 |
| Transmittance | 1毫米 | % | ISO 13468-2 | 89 |
| Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Constant | 23℃/50%r.h 100Hz | -- | IEC 60250 | 3.1 |
| 23℃/50%r.h 1MHz | -- | IEC 60250 | 3.0 | |
| Dissipation Factor? | 23℃/50%r.h 100Hz | 10-4 | IEC 60250 | |
| 23℃/50%r.h 1MHz | 10-4 | IEC 60250 | ||
| Volume Resistivity | 23℃/50%r.h | Ohm.m | IEC 60093 | |
| Surface Resistivity | 23℃/50%r.h | Ohm | IEC 60093 | |
| Dielectric Strength | 23℃/50%r.h 1毫米 | kv/毫米 | IEC 60243-1 | 34 |
| Comparative Tracking Index | 23℃/50%r.h 方法A | 等级 | IEC 60112 | 250 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.