PC Makrolon® 1837 012475 COVESTRO SHANGHAI

Unit Price:
$6821 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility High impact resistance High hardness
Application Areas:Automotive interior parts Washing machine
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow	ISO 2577	0.60 到 0.80	%
	Modeling Shrinkage	流量	ISO 2577	0.60 到 0.80	%
		Modeling Shrinkage	Across Flow : 280°C, 2.00 mm 4	ISO 294-4	0.70	%
		Modeling Shrinkage	Modeling Shrinkage	流量 : 2.00 mm 4	ISO 294-4	0.65	%
Moisture Absorption	Saturation, 23°C	ISO 62	0.40	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.12	%
Melt Mass-Flow Rate	300°C/1.2 kg	ISO 1133	12	g/10 min
Melt Volume flow Rate	300°C/1.2 kg	ISO 1133	11.0	cm3/10min
Apparent Density		ISO 60	0.64	g/cm³
Density	23°C	ISO 1183	1.19	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Strain at Flexural Strength	23°C	ISO 178	6.8	%
Flexural Stress	23°C	ISO 178	86.0	Mpa
Flexural Stress	Flexural Stress	3.5% Strain, 23°C	ISO 178	68.0	Mpa
Tensile Stress	Yield, 23°C	ISO 527-2/50	58.0	Mpa
Tensile Stress	Tensile Stress	Break, 23°C	ISO 527-2/50	60.0	Mpa
Tensile Strain	Yield, 23°C	ISO 527-2/50	5.7	%
Tensile Strain	Tensile Strain	Break, 23°C	ISO 527-2/50	120	%
Tensile Modulus	23°C	ISO 527-2/1	2200	Mpa
Flexural Modulus	23°C	ISO 178	2200	Mpa
Nominal Tensile Strain at Break	23°C	ISO 527-2/50	> 50	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Thermal Conductivity	23°C	ISO 8302	0.20	W/m/K
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	134	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	121	°C
Vicat Softening Temperature	--	ISO 306/B50	141	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	143	°C
Glass Transition Temperature		ISO 11357-2	143	°C
Linear thermal expansion coefficient	Flow : 23 to 55°C	ISO 11359-2	7.0E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 55°C	ISO 11359-2	7.0E-5	cm/cm/°C
Ball PressureTest	134°C	IEC 60695-10-2	通过

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	23°C, 1.00 mm	IEC 60243-1	34	KV/mm
Relative Permittivity	23°C, 100 Hz	IEC 60250	3.20
Relative Permittivity	Relative Permittivity	23°C, 1 MHz	IEC 60250	3.10
Comparative Tracking Index	Solution A	IEC 60112	225	V
Comparative Tracking Index	Comparative Tracking Index	Solution B	IEC 60112	100	V
Dissipation Factor?	23°C, 100 Hz	IEC 60250	1.4E-3
Dissipation Factor?	Dissipation Factor?	23°C, 1 MHz	IEC 60250	0.013
Surface Resistivity		IEC 60093	1.0E+16	ohms
Volume Resistivity	23°C	IEC 60093	1.0E+16	ohms·cm

Injection	Test Result	Unit
Suggested Max Moisture	< 0.020	%
Processing (Melt) Temp	280 到 320	°C
Mold Temperature	70 到 110	°C
Suggested Shot Size	30 到 70	%
Rear Temperature	250 到 270	°C
Middle Temperature	270 到 290	°C
Front Temperature	285 到 305	°C
Nozzle Temperature	270 到 305	°C
Back Pressure	10.0 到 20.0	Mpa
Vent Depth	0.025 到 0.075	mm
Drying Temperature ()	120	°C
Dry Air Dryer	4.0	hr

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-60°C	ISO 179/1eU	无断裂
	Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	无断裂
	Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	无断裂
Multi-Axial Instrumented Impact Energy	-30°C	ISO 6603-2	55.0	J
Multi-Axial Instrumented Impact Energy	Multi-Axial Instrumented Impact Energy	23°C	ISO 6603-2	50.0	J
Multi-Axial Instrumented Impact Peak Force	-30°C	ISO 6603-2	5800	N
Multi-Axial Instrumented Impact Peak Force	Multi-Axial Instrumented Impact Peak Force	23°C	ISO 6603-2	4900	N
Charpy Notched Impact Strength	-30°C, Partial Break	ISO 179/1eA	50	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C, Partial Break	ISO 179/1eA	60	kJ/m²
Notched Izod Impact Strength	-30°C, Partial Break	ISO 180/A	45	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C, Partial Break	ISO 180/A	60	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness		ISO 2039-1	104	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	0.75 mm	IEC 60695-2-12	850	°C
	Glow Wire Flammability Index	1.5 mm	IEC 60695-2-12	875	°C
	Glow Wire Flammability Index	Glow Wire Flammability Index	3.0 mm	IEC 60695-2-12	900	°C
Glow Wire Ignition Temperature	1.5 mm	IEC 60695-2-13	825	°C
	Glow Wire Ignition Temperature	2.0 mm	IEC 60695-2-13	825	°C
	Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0 mm	IEC 60695-2-13	850	°C
Burning Rate	> 1.00 mm	ISO 3795	passed
Flame Rating	0.75 mm	UL 94	HB
ISO Shortname			ISO 7391-PC,MP,(,,)-09-9
Oxygen Index		ISO 4589-2	30	%
Flash Ignition Temperature		ASTM D1929	450	°C
Needle Flame Test	1.50 mm 11	IEC 60695-11-5	5.0	sec
	Needle Flame Test	1.50 mm 12	IEC 60695-11-5	120.0	sec
		Needle Flame Test	2.00 mm 11	IEC 60695-11-5	5.0	sec
			Needle Flame Test	2.00 mm 12	IEC 60695-11-5	120.0	sec
				Needle Flame Test	3.00 mm 11	IEC 60695-11-5	10.0	sec
				Needle Flame Test	Needle Flame Test	3.00 mm 12	IEC 60695-11-5	120.0	sec
Self Ignition Temperature		ASTM D1929	530	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.