PBT VALOX™ V4860HR BK1066 SABIC INNOVATIVE JAPAN
127
- Unit Price:
- $9307 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Dimensional stability
- Application Areas:Automotive Applications Lighting fixtures
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ASTMD792 | 1.64 | g/cm³ | |
| ISO1183 | 1.64 | g/cm³ | ||
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.060 | % |
| Saturation,23°C | ISO62 | 0.19 | % | |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.50to1.0 | % |
| MD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 12.4 | cm3/10min |
| Melt mass flow rate | 250°C/5.0kg | ASTMD1238 | 18 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break | ISO527-2/5 | 111 | Mpa |
| Elongation rate 3 | Yield | ASTMD638 | 2.3 | % |
| Tensile strain | Yield | ISO527-2/5 | 2.1 | % |
| Elongation rate 4 | Break | ASTMD638 | 2.3 | % |
| Tensile strain | Break | ISO527-2/5 | 2.2 | % |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 6740 | Mpa |
| Bending modulus 5 | ISO178 | 7880 | Mpa | |
| Bending stress 5 | --6 | ISO178 | 182 | Mpa |
| --7 | ISO178 | 183 | Mpa | |
| Tensile strength 3 | Break | ASTMD638 | 115 | Mpa |
| Tensile stress | Yield | ISO527-2/5 | 112 | Mpa |
| Tensile strength 3 | Yield | ASTMD638 | 116 | Mpa |
| Tensile modulus | ISO527-2/1 | 9450 | Mpa | |
| Tensile modulus 2 | ASTMD638 | 9750 | Mpa | |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 174 | Mpa |
| Bending strength 5 | Break,50.0mmSpan | ASTMD790 | 2.96 | Mpa |
| Fracture bending strain 8 | ISO178 | 2.9 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 197 | °C |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 205 | °C | |
| Hot deformation temperature 11 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 188 | °C |
| Vicat softening temperature | ASTMD152512 | 176 | °C | |
| -- | ISO306/B50 | 176 | °C | |
| -- | ISO306/B120 | 175 | °C | |
| BallPressureTest13 | 75°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40to95°C | ASTME831 | 2.4E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 2.3E-05 | cm/cm/°C | |
| TD：-40to95°C | ASTME831 | 1.1E-04 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 221 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| CharpyNotchedImpactStrength9 | 23°C | ISO179/1eA | 11 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 74 | J/m |
| 23°C | ASTMD256 | 90 | J/m | |
| Suspended wall beam gap impact strength 10 | -30°C | ISO180/1A | 8.5 | kJ/m² |
| 23°C | ISO180/1A | 10 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 13.4 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.8mm,TestingbySABIC | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.