Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Across Flow | ISO 294-4 | 0.60 | % |
Modeling Shrinkage | 流量 | ISO 294-4 | 0.30 | % |
Moisture Absorption | Saturation, 23°C | ISO 62 | 0.044 | % |
Moisture Absorption | Equilibrium, 23°C, 50% RH | ISO 62 | 0.015 | % |
Density | | ISO 1183 | 1.67 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Stress | 23°C | ISO 178 | 225 | Mpa |
Tensile Stress | Break | ISO 527-2/1A/5 | 150 | Mpa |
Tensile Strain | Break | ISO 527-2/1A/5 | 1.3 | % |
Tensile Modulus | | ISO 527-2/1A | 16000 | Mpa |
Flexural Modulus | 23°C | ISO 178 | 15700 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 260 | °C |
Melting Temperature | | ISO 11357-3 | 335 | °C |
Linear thermal expansion coefficient | Flow | ISO 11359-2 | 8.0E-6 | cm/cm/°C |
Linear thermal expansion coefficient | Across Flow | ISO 11359-2 | 3.1E-5 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | | IEC 60243-1 | 33 | KV/mm |
Relative Permittivity | 1 MHz | IEC 60250 | 3.50 | |
Surface Resistivity | | IEC 60093 | 1.0E+17 | ohms |
Volume Resistivity | | IEC 60093 | 1.0E+16 | ohms·cm |
Dissipation Factor? | 1 MHz | IEC 60250 | 0.016 | |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Temperature | | | 150 | °C |
Suggested Max Moisture | | | 0.010 | % |
Processing (Melt) Temp | | | 335 到 345 | °C |
Mold Temperature | | | 80 到 120 | °C |
Drying Time | | | 4.0 到 24 | hr |
Rear Temperature | | | 315 到 325 | °C |
Middle Temperature | | | 320 到 330 | °C |
Front Temperature | | | 325 到 335 | °C |
Nozzle Temperature | | | 335 到 345 | °C |
Back Pressure | | | < 3.00 | Mpa |
Hopper Temperature | | | 20 到 30 | °C |
Injection Rate | | | 快速 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | 23°C | ISO 180/1A | 9.0 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.