Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD:2.00mm | 内部方法 | 0.40 | % |
| Modeling Shrinkage | MD:2.00mm | 内部方法 | 0.40 | % |
| Melt Volume flow Rate | 260°C/2.16kg | ISO1133 | 20.0 | cm3/10min |
| Spiral Flow | | 内部方法 | 40.0 | CM |
| Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.10 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Nominal Tensile Strain at Break | | ISO527-2 | 50 | % |
| Tensile Stress | Yield | ISO527-2 | 64.0 | Mpa |
| Flexural Modulus | | ISO178 | 3000 | Mpa |
| Flexural Stress | | ISO178 | 90.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 78.0 | °C |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 88.0 | °C |
| RTIElec | | UL746 | 60.0 | °C |
| Evolution Calendar intelligent importer | | UL746 | 60.0 | °C |
| RTIStr | | UL746 | 60.0 | °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 5.8E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | | IEC60243-1 | 36 | KV/mm |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.58mm | UL94 | V-1 | |
| UL flame retardant rating | 1.0mm | UL94 | V-0 | |
| UL flame retardant rating | 0.8mm | UL94 | 5VB | |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| ISO Shortname | | | >PC+ABS-FR(40)< | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.