PBT Crastin® S600F10 NC010 DuPont, European Union
49
- Unit Price:
- $2345 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high viscosity
- Application Areas:Electronic and electrical
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO294-4 | 1.7 | % |
| MD | ISO294-4 | 1.7 | % | |
| -，Across Flow | % | ISO 294-4 | 1.6 | |
| -，Flow | % | ISO 294-4 | 1.7 | |
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 0.50 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
| -，23C/59RH | % | ISO 62 | 0.2 | |
| -，Sat/23C | % | ISO 62 | 0.5 | |
| Melt Mass-Flow Rate | 250°C/2.16kg | ISO1133 | 10 | g/10min |
| MediumDensity | 1.11 | g/cm³ | ||
| Ejection Temperature | 170 | °C | ||
| SpecificHeatCapacityofMelt | 2100 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.21 | W/m/K | ||
| Density / Specific Gravity | g/cm | ISO 1183 | 1.30 | |
| ISO1183 | 1.30 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress (Yield) | 23℃ | MPa | ISO 527-1, -2 | 57 |
| Tensile Strain (Yield) | 23℃ | % | ISO 527-1, -2 | |
| Tensile Strain (Break) | 23℃ | % | ISO 527-1, -2 | |
| Tensile Strain (Break) | 23 ℃, 50 mm/min | % | ISO 527-1, -2 | |
| Nominal Tensile Strain at Break | ISO527-2 | >50 | % | |
| Charpy Notched Impact Strength | -，-30℃, Type 1, Edgewise | KJ/m | ISO 179 | No Break |
| -，23℃, Type 1, Edgewise | KJ/m | ISO 179 | No Break | |
| Charpy Notched Impact Strength | -，-30 ℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | |
| -，23 ℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | 5.4 | |
| Unnotched Izod Impact Strength | 23 ℃, Type 1 | KJ/m | ISO 180 | No Break |
| Tensile Stress | Yield | ISO527-2 | 57.0 | Mpa |
| Tensile Strain | Yield | ISO527-2 | 4.0 | % |
| Flexural Stress | ISO178 | 85.0 | Mpa | |
| Notched Impact Strength | 23 ℃, Type 1, Notch A | KJ/m | ISO 180 | |
| Tensile Creep Modulus | -，1h | MPa | ISO 899-1 | 2600 |
| -，1000h | MPa | ISO 899-1 | 1800 | |
| 1000hr | ISO899-1 | 1800 | Mpa | |
| Tensile Modulus | 23℃ | MPa | ISO 527-1, -2 | 2700 |
| ISO527-2 | 2600 | Mpa | ||
| Flexural Modulus | ISO178 | 2300 | Mpa | |
| Flexural Strength | 23℃ | MPa | ISO 178 | 85 |
| Tensile Creep Modulus | 1hr | ISO899-1 | 2300 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ISO306/B50 | 175 | °C | |
| Melting Temperature | ISO11357-3 | 224 | °C | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 115 | °C |
| 0.45MPa,Annealed | ISO75-2/B | 180 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 50.0 | °C | |
| 1.8MPa,Annealed | ISO75-2/A | 60.0 | °C | |
| -，0.45 Mpa，Unannealed | ℃ | ISO 75B-1, -2 | 160 | |
| -，1.8Mpa，Unannealed | ℃ | ISO 75A-1, -2 | ||
| Flame retardancy | 1.50 mm | UL94 | HB | |
| 3.00 mm | UL 94 | HB | ||
| 0.750 mm | UL 94 | HB | ||
| Linear thermal expansion coefficient | MD：-- | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 8E-05 | cm/cm/°C | |
| MD：55to160°C | ISO11359-2 | 1.9E-04 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 2E-04 | cm/cm/°C | |
| Melting temperature | ℃ | ISO 3146 | 225 | |
| Glass Transition Temperature | ISO11357-2 | 55.0 | °C | |
| Coefficient of Linear Thermal Expansion | 平行Flow ，23 to 55℃ (73 to 130°F) | cm/cm/℃ | ISO 11359-1, -2 | 0.00013 |
| 垂直Flow ，23 to 55℃ (73 to 130°F) | cm/cm/℃ | ISO 11359-1, -2 | 0.00013 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative Permittivity | 100Hz | IEC60250 | 3.60 | |
| 1MHz | IEC60250 | 3.20 | ||
| Comparative Tracking Index | IEC60112 | 400 | V | |
| Dissipation Factor? | 100Hz | IEC60250 | 1E-03 | |
| 1MHz | IEC60250 | 0.020 | ||
| Dielectric Strength | -- | IEC60243-1 | 26 | KV/mm |
| 1.00mm3 | IEC60243-1 | 26 | KV/mm | |
| 2.00mm4 | IEC60243-1 | 15 | KV/mm | |
| Surface Resistivity | IEC60093 | 1E+15 | ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Notched Izod impact strength | -30°C | ISO180/1U | 130 | kJ/m² |
| 23°C | ISO180/1U | NoBreak | ||
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 4.0 | kJ/m² |
| 23°C | ISO179/1eA | 5.0 | kJ/m² | |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 5.0 | kJ/m² |
| 23°C | ISO180/1A | 5.0 | kJ/m² |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen Index | % | ISO 4589-1, -2 | 22 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 3.0mm | IEC60695-11-10,-20 | HB | ||
| Oxygen Index | ISO4589-2 | 22 | % | |
| FMVSS Flammability | FMVSS302 | SE |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 145 | µgC/g | |
| Odor | VDA270 | 3.00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.