Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 230℃ 2.16kg | ISO 1133 | 7 | g/10min |
proportion | | ISO 1183 | 900-910 | kg/m3 |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | 23℃ | ASTM D256 | NB | |
Notched Izod Impact Strength | -20℃ | ASTM D256 | 110 | J/m |
Tensile Modulus | I.Omm/min | ISO 527 | 1200 | Mpa |
Tensile Strength | Yield50mmzmin | ISO 527 | 22 | Mpa |
Tensile Elongation | Yield50mm/min | ISO 527 | 6 | % |
Flexural Modulus | | ISO 178 | 1250 | Mpa |
Charpy Notched Impact Strength | 23°C1eA型 | ISO 179 | NB | |
Charpy Notched Impact Strength | -20°C1eA型 | ISO 179 | 9 | kJ/m² |
Charpy Notched Impact Strength | -30℃1eA型 | ISO 179 | 7 | kJ/m² |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa | ISO 75 | 90 | °C |
Vicat Softening Temperature | 10N | ISO 306 | 142 | °C |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R标尺 | ISO 2039 | 87 | |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Melting temperature | | | 220-260 | °C |
Mold Temperature | | | 10-40 | °C |
Injection Rate | | | 超高速 | |
Holding Pressure | | | 200-500 | Bar |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.