Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | | 内部方法 | 3.4 | % |
| Apparent Density | | ISO60 | 0.82 | g/cm³ |
| Particle Size Distribution | | ISO13320 | 450 | µm |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | 23°C | ISO527-2 | 650 | Mpa |
| Heat Deflection Temperature | 15MPa2 | ASTMD621 | 8.00 | % |
| Heat Deflection Temperature | 15MPa3 | ASTMD621 | 9.00 | % |
| Heat Deflection Temperature | 15MPa4 | ASTMD621 | 4.00 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Thermal Conductivity | | DIN52612 | 0.22 | W/m/K |
| Linear thermal expansion coefficient | MD：30to100°C | DIN53752 | 1.2E-04 | cm/cm/°C |
| Linear thermal expansion coefficient | MD：30to200°C | DIN53752 | 1.4E-04 | cm/cm/°C |
| Linear thermal expansion coefficient | MD：30to260°C | DIN53752 | 1.7E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | 0.200mm | ISO12086 | 78 | KV/mm |
| Surface Resistivity | | IEC60093 | 1E+17 | ohms |
| Volume Resistivity | | IEC60093 | 1E+18 | ohms·cm |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation | Break,200μm | ISO527-3 | 600 | % |
| Tensile Strength | 200µm | ISO527-3 | 37.0 | Mpa |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | Shore D | ISO868 | 59 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.