Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Transparent level

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow : 23°C, 2.00 mm	ISO 294-4	0.90	%
Modeling Shrinkage	Modeling Shrinkage	流量 : 23°C, 2.00 mm	ISO 294-4	0.40	%
Moisture Absorption	24 hr, 23°C	ISO 62	0.90	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	1.9	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Break, 23°C	ISO 527-2	195	Mpa
Tensile Strain	Break, 23°C	ISO 527-2	3.0	%
Tensile Modulus	23°C	ISO 527-2	10000	Mpa
Flexural Modulus	23°C	ISO 178	9600	Mpa
Flexural Stress	23°C	ISO 178	270	Mpa
Poisson's Ratio	23°C	ISO 527	0.40

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Linear thermal expansion coefficient	Flow : 23 to 55°C, 2.00 mm	ISO 11359-2	2.2E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 55°C, 2.00 mm	ISO 11359-2	1.1E-4	cm/cm/°C
Melting temperature		ISO 11357-3	260	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	260	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	250	°C
RTI	0.75 mm	UL 746	115	°C
	RTI	1.5 mm	UL 746	120	°C
	RTI	RTI	3.0 mm	UL 746	120	°C
RTI Imp	0.75 mm	UL 746	85.0	°C
	RTI Imp	1.5 mm	UL 746	85.0	°C
	RTI Imp	RTI Imp	3.0 mm	UL 746	105	°C
RTI Elec	0.75 mm	UL 746	120	°C
	RTI Elec	1.5 mm	UL 746	120	°C
	RTI Elec	RTI Elec	3.0 mm	UL 746	120	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
High Amp Arc Ignition	0.75 mm	UL 746	PLC 0
	High Amp Arc Ignition	1.5 mm	UL 746	PLC 0
	High Amp Arc Ignition	High Amp Arc Ignition	3.0 mm	UL 746	PLC 0
Arc Resistance	3.00 mm	ASTM D495	5.00	sec
Volume Resistivity	0.750 mm	IEC 60093	1.0E+13	ohms·cm
Dielectric Strength	1.00 mm	IEC 60243	24	KV/mm
Comparative Tracking Index	3.00 mm	IEC 60112	600	V
Hot-wire Ignition	0.75 mm	UL 746	PLC 4
	Hot-wire Ignition	1.5 mm	UL 746	PLC 4
	Hot-wire Ignition	Hot-wire Ignition	3.0 mm	UL 746	PLC 4
High Voltage Arc Tracking Rate		UL 746	PLC 1

Injection	Test Result	Unit
Suggested Max Regrind	25	%
Drying Temperature	80	°C
Processing (Melt) Temp	285 到 305	°C
Mold Temperature	65 到 95	°C
Drying Time	4.0	hr
Rear Temperature	280 到 310	°C
Middle Temperature	280 到 310	°C
Front Temperature	280 到 310	°C
Nozzle Temperature	280 到 310	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO 179	65	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179	75	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
Burning Rate	2.00 mm, 自动灭火	ISO 3795	0.0	mm/min
Flame Rating	0.75 mm	UL 94	HB
	Flame Rating	1.5 mm	UL 94	HB
	Flame Rating	Flame Rating	3.0 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.