PC/PBT VALOX™ 420SE0-1001 SABIC INNOVATIVE NANSHA

Unit Price:
$3866 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
73MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow，3.2-4.6mm	SABIC method	0.6-1	%
	Modeling Shrinkage	Flow, 1.5-3.2 mm	SABIC method	0.3 - 0.5	%
	Modeling Shrinkage	Modeling Shrinkage	Flow，3.2-4.6 mm	SABIC method	0.5 - 0.8	%
Moisture Absorption	24 hours	ASTM D 570	0.06	%
Modeling Shrinkage	Across Flow ,1.5-3.2 mm	SABIC method	0.4 - 0.6	%
Modeling Shrinkage	Modeling Shrinkage	Flow，3.2 mm	SABIC method	0.5 - 0.7	%
proportion		ASTM D 792	1.61	—
Specific Volume		ASTM D 792	0.62	cm³/g

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Elongation	Yield,类型L, 5 mm/min	ASTM D 638	1.2	%
Tensile Elongation	Tensile Elongation	Break，类型L, 5 mm/min	ASTM D 638	1.2	%
抗张程度	Yield，类型L，5 mm/min	ASTM D 638	95	Mpa
抗张程度	抗张程度	Break，类型L, 5 mm/min	ASTM D 638	95	Mpa
Tensile Modulus	5 mm/min	ASTM D 638	11500	Mpa
Rockwell Hardness	R		119	-
Flexural Strength	Break,1.3 mm/min, 50 mm span	ASTM D 790	186	Mpa
Flexural Modulus	1.3 mm/min, 50 mm span	ASTM D 790	9400	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
HDT（热变形温度）	0.45 MPa, 3.2 mm, Unannealed	ASTM D 648	212	°C
	HDT（热变形温度）	1.82 MPa, 3.2mm, Unannealed	ASTM D 648	200	°C
		HDT（热变形温度）	0.45 MPa, 6.4 mm，Unannealed	ASTM D 648	215	°C
		HDT（热变形温度）	HDT（热变形温度）	1.82 MPa, 6.4 mm, Unannealed	ASTM D 648	204	°C
CTE （线形膨胀系数）	-40℃-4O℃, Flow	ASTM E 831	0.0000252	1/℃
CTE （线形膨胀系数）	CTE （线形膨胀系数）	60℃-138℃, Flow	ASTM E 831	0.0000252	1/℃

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.