PA6/66 Ultramid® A3WG6 BK 00546 BASF GERMANY
52
- Unit Price:
- $4237 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Across Flow | ISO 294-4 | 1.2 | % |
| 流量 | ISO 294-4 | 0.40 | % | |
| Moisture Absorption | Saturation, 23°C | ISO 62 | 5.6 到 6.3 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 1.5 到 1.9 | % | |
| Apparent Density | 0.70 | g/cm³ | ||
| Viscosity number | 96% H2SO4 | ISO 307 | 160 | cm³/g |
| Melt Volume flow Rate | 275°C/5.0 kg | ISO 1133 | 10.0 | cm3/10min |
| Modeling Shrinkage | 0.40 到 0.50 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | ISO 178 | 285 | Mpa | |
| Tensile Modulus | ISO 527-2 | 9500 | Mpa | |
| Flexural Modulus | ISO 178 | 9200 | Mpa | |
| Tensile Stress | Break | ISO 527-2 | 185 | Mpa |
| Tensile Strain | Break | ISO 527-2 | 3.7 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 260 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 245 | °C | |
| Melting temperature | ISO 11357-3 | 260 | °C | |
| Polymer Abbreviation | PA66-GF30 |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Time | 4.0 | hr | ||
| Rear Temperature | 290 | °C | ||
| Middle Temperature | 290 | °C | ||
| Front Temperature | 290 | °C | ||
| Nozzle Temperature | 290 | °C | ||
| Hopper Temperature | 80 | °C | ||
| Residence Time | < 10.0 | min | ||
| Screw Speed | < 18 | m/min | ||
| Drying Temperature | 80 | °C | ||
| Suggested Max Moisture | 0.15 | % | ||
| Processing (Melt) Temp | 280 到 300 | °C | ||
| Mold Temperature | 80 到 90 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 75 | kJ/m² |
| 23°C | ISO 179/1eU | 90 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.