Technical Data Sheet
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Coefficient of Friction | | ASTM D-1894 | 0.16-0.2 | |
| Tensile Elongation (Break MD) | 50um | ASTM D-882 | 450 | % |
| Tensile Elongation (Break TD) | 50um | ASTM D-882 | 650 | % |
| Elmendorf Tear Strength (TD) | 50um | ASTM D-1922 | 400 | g |
| Elmendorf Tear Strength (MD) | 50um | ASTM D-1922 | 500 | g |
| Secant Modulus (MD) | 2% Secant，50um | ASTM D-882 | 190 | Mpa |
| Secant Modulus (TD) | 2% Secant，50um | ASTM D-882 | 175 | Mpa |
| Tensile Strength (Break TD) | 50um | ASTM D-882 | 15 | Mpa |
| Tensile Strength (Break TD) | 50um | ASTM D-882 | 17 | Mpa |
| Tensile Strength (Yield TD) | 50um | ASTM D-882 | 9 | Mpa |
| Tensile Strength (Yield MD) | 50um | ASTM D-882 | 9 | Mpa |
| Gardner Impact | 50um | ASTM D-1709A | 120 | g |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ISO 306/A | 93 | °C |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Temperature | | | 150-170 | °C |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Gloss | 20°，50um | ASTM D-2457 | 70 | |
| Haze | 50um | ASTM D-1003 | 7 | % |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 190℃/2.16kg | ISO 1133 | 3.5 | g/10min |
| Density | | ASTM D-792 | 0.923 | g/m3 |
| Film Thickness | | | 50 | um |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.