PA6/6T Ultramid® KR4340G6 BASF GERMANY
113
- Unit Price:
- $6602 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 40.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low water absorption Rigidity and strength
- Application Areas:Electronic and Electrical Automotive components
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow | ISO 294-4 | 0.70 | % |
| 流量 | ISO 294-4 | 0.30 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 4.3 到 5.3 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 1.4 到 1.8 | % | |
| Apparent density | 0.70 | g/cm³ | ||
| Stickiness number | 96% H2SO4 | ISO 307 | 120 | cm³/g |
| Molten Volume Flow Rate (MVR) | 325°C/5.0 kg | ISO 1133 | 45.0 | cm3/10min |
| Mold Shrinkage - Model Heating | 1.50 mm | 0.10 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break | ISO 527-2 | 150 | Mpa |
| Tensile strain | Break | ISO 527-2 | 2.5 | % |
| Tensile modulus | ISO 527-2 | 11000 | Mpa | |
| Bending modulus | ISO 178 | 11000 | Mpa | |
| Bending stress | ISO 178 | 240 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature | ISO 11357-3 | 290 | °C | |
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 220 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | -- | ohms | |
| Volume resistivity | IEC 60093 | 1.0E+17 | ohms·cm | |
| Dissipation factor | 1 MHz | IEC 60250 | 0.015 | |
| Relative permittivity | 1 MHz | IEC 60250 | 3.90 | |
| Leakage Trace Index | Solution A | IEC 60112 | 600 | V |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying time | 8.0 | hr | ||
| Temperature at the rear of the barrel | 300 | °C | ||
| Temperature in the middle of the barrel | 310 | °C | ||
| Temperature at the front of the material cylinder | 320 | °C | ||
| Spray nozzle temperature | 320 | °C | ||
| Hopper temperature | 80 | °C | ||
| Residence Time | < 5.0 | min | ||
| Screw Speed | < 18 | m/min | ||
| drying temperature | 110 | °C | ||
| Suggested maximum moisture content | 0.030 | % | ||
| Processing (melt) temperature | 310 到 330 | °C | ||
| Mold temperature | 80 到 120 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 65 | kJ/m² |
| 23°C | ISO 179/1eU | 65 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Polymer Abbreviation | PA6T/6-GF30 FR | |||
| Burning wire flammability index | 0.40 mm | IEC 60695-2-12 | 960 | °C |
| Extreme Oxygen Index | ISO 4589-2 | 50 | % | |
| Hot filament ignition temperature | 0.40 mm | IEC 60695-2-13 | 775 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.