PBT Crastin® SK601 BK851 DUPONT TAIWAN
62
- Unit Price:
- $2636 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Filler: Glass fiber reinf Good strength (glass fibe 20% by weight ratio) 20% filler by weight Good strength (glass fibe 20% by weight ratio) 20% filler by weight
- Application Areas:Electronic and electrical Industrial applications Automotive Applications Automotive Applications
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO294-4 | 1.1 | % |
| MD | ISO294-4 | 0.30 | % | |
| -，Across Flow | % | ISO 294-4 | 1.0 | |
| -，Flow | % | ISO 294-4 | ||
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 0.40 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.15 | % | |
| -，23C/59RH | % | ISO 62 | 0.15 | |
| -，Sat/23C | % | ISO 62 | ||
| MediumDensity | 1.26 | g/cm³ | ||
| Ejection Temperature | 170 | °C | ||
| SpecificHeatCapacityofMelt | 1860 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.25 | W/m/K | ||
| Density / Specific Gravity | ISO1183 | 1.45 | g/cm³ | |
| g/cm | ISO 1183 | 1.45 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -，-30℃, Type 1, Edgewise | KJ/m | ISO 179 | 54 |
| -，23 ℃, Type 1, Edgewise | KJ/m | ISO 179 | 56 | |
| Charpy Notched Impact Strength | -，-30 ℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | 9.8 |
| -，23℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | 7.5 | |
| Unnotched Izod Impact Strength | 23 ℃, Type 1 | KJ/m | ISO 180 | 44 |
| Tensile Creep Modulus | 1hr | ISO899-1 | 7200 | Mpa |
| Tensile Strain (Break) | 23℃ | % | ISO 527-1, -2 | 3.2 |
| Tensile Stress (Break) | 23℃ | MPa | ISO 527-1, -2 | |
| Tensile Stress | Break | ISO527-2 | 120 | Mpa |
| Tensile Strain | Break | ISO527-2 | 3.2 | % |
| Flexural Stress | ISO178 | 180 | Mpa | |
| Notched Impact Strength | 23 ℃, Type 1, Notch A | KJ/m | ISO 180 | |
| Tensile Creep Modulus | -，1h | MPa | ISO 899-1 | 7200 |
| -，1000h | MPa | ISO 899-1 | ||
| 1000hr | ISO899-1 | 5600 | Mpa | |
| Tensile Modulus | 23℃ | MPa | ISO 527-1, -2 | 7400 |
| ISO527-2 | 7000 | Mpa | ||
| Flexural Modulus | ISO178 | 6500 | Mpa | |
| 23℃ | MPa | ISO 178 | 6200 | |
| Flexural Strength | 23℃ | MPa | ISO 178 | 180 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 204 | °C | |
| -，0.45 Mpa，Unannealed | ℃ | ISO 75B-1, -2 | ||
| -，1.80 Mpa，Unannealed | ℃ | ISO 75B-1, -2 | 204 | |
| Flame Rating | -，0.750 mm | UL 94 | HB | |
| -，1.50 mm | UL 94 | HB | ||
| -，3.00 mm | UL 94 | HB | ||
| Linear thermal expansion coefficient | MD | ISO11359-2 | 4E-05 | cm/cm/°C |
| TD | ISO11359-2 | 1E-04 | cm/cm/°C | |
| Melting temperature | ℃ | ISO 3146 | 225 | |
| Vicat Softening Temperature | ISO306/B50 | 210 | °C | |
| Melting Temperature | ISO11357-3 | 224 | °C | |
| Coefficient of Linear Thermal Expansion | 平行Flow ，23 to 55℃(73 to 130°F) | cm/cm/℃ | ISO 11359-1, -2 | |
| 垂直Flow ，23 to 55℃(73 to 130°F) | cm/cm/℃ | ISO 11359-1, -2 | 0.000040 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative Permittivity | 100Hz | IEC60250 | 4.00 | |
| 1MHz | IEC60250 | 3.60 | ||
| Comparative Tracking Index | IEC60112 | 350 | V | |
| Dissipation Factor? | 100Hz | IEC60250 | 1.2E-03 | |
| 1MHz | IEC60250 | 0.019 | ||
| Dielectric Strength | IEC60243-1 | 29 | KV/mm | |
| Surface Resistivity | IEC60093 | 1E+15 | ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod impact strength | -30°C | ISO180/1U | 60 | kJ/m² |
| 23°C | ISO180/1U | 60 | kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 55 | kJ/m² |
| 23°C | ISO179/1eU | 60 | kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 9.0 | kJ/m² |
| 23°C | ISO179/1eA | 8.0 | kJ/m² | |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 8.0 | kJ/m² |
| 23°C | ISO180/1A | 9.0 | kJ/m² |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen Index | % | ISO 4589-1, -2 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Oxygen Index | ISO4589-2 | 19 | % | |
| FMVSS Flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate)4 | ISO6452 | 1E-04 | g |
| Burning Rate | 1.00mm | ISO3795 | 28 | mm/min |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 140 | µgC/g | |
| Odor | VDA270 | 3.00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.