Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:23°C,2.00mm | ISO294-4 | 0.90 | % |
Modeling Shrinkage | MD:23°C,2.00mm | ISO294-4 | 0.40 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.90 | % |
Moisture Absorption | Equilibrium,50%RH | ISO62 | 1.9 | % |
Density / Specific Gravity | | ISO1183 | 1.37 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Fish 'sratio' | 23°C | ISO527 | 0.40 | |
Tensile Modulus | 23°C | ISO527-2 | 10000 | Mpa |
Flexural Modulus | 23°C | ISO178 | 9600 | Mpa |
Tensile Stress | Break,23°C | ISO527-2 | 195 | Mpa |
Tensile Strain | Break,23°C | ISO527-2 | 3.0 | % |
Flexural Stress | 23°C | ISO178 | 270 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
RTIElec | 0.75mm | UL746 | 140 | °C |
RTIElec | 1.5mm | UL746 | 140 | °C |
RTIElec | 3.0mm | UL746 | 140 | °C |
Evolution Calendar intelligent importer | 0.75mm | UL746 | 120 | °C |
Evolution Calendar intelligent importer | 1.5mm | UL746 | 120 | °C |
Evolution Calendar intelligent importer | 3.0mm | UL746 | 120 | °C |
RTIStr | 0.75mm | UL746 | 125 | °C |
RTIStr | 1.5mm | UL746 | 140 | °C |
RTIStr | 3.0mm | UL746 | 140 | °C |
Linear thermal expansion coefficient | MD:23to55°C,2.00mm | ISO11359-2 | 2.2E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:23to55°C,2.00mm | ISO11359-2 | 1.1E-04 | cm/cm/°C |
Melting temperature | | ISO11357-3 | 260 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 260 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 250 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Arc Resistance | 3.00mm | ASTMD495 | PLC6 | |
High Voltage Arc Tracking Rate | HVTR | UL746 | PLC1 | |
Dielectric Strength | 1.00mm | IEC60243 | 20 | KV/mm |
Comparative Tracking Index | 3.00mm | IEC60112 | 250to399 | V |
Volume Resistivity | 3.00mm | IEC60093 | 1E+13 | ohms·cm |
High Amp Arc Ignition | 0.75mm | UL746 | PLC0 | |
High Amp Arc Ignition | 1.5mm | UL746 | PLC0 | |
High Amp Arc Ignition | 3.0mm | UL746 | PLC0 | |
Hot-wire Ignition | 0.75mm | UL746 | PLC4 | |
Hot-wire Ignition | 1.5mm | UL746 | PLC3 | |
Hot-wire Ignition | 3.0mm | UL746 | PLC4 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179 | 65 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179 | 75 | kJ/m² |
Charpy Notched Impact Strength | -30°C | ISO179 | 10 | kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO179 | 11 | kJ/m² |
Notched Izod Impact Strength | -30°C | ISO180 | 10 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180 | 12 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.75mm | UL94 | HB | |
UL flame retardant rating | 1.5mm | UL94 | HB | |
UL flame retardant rating | 3.0mm | UL94 | HB | |
Glow Wire Flammability Index | 0.75mm | IEC60695-2-12 | 675 | °C |
Glow Wire Flammability Index | 1.5mm | IEC60695-2-12 | 675 | °C |
Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 675 | °C |
Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 700 | °C |
Glow Wire Ignition Temperature | 0.75mm | IEC60695-2-13 | 700 | °C |
Glow Wire Ignition Temperature | 1.5mm | IEC60695-2-13 | 700 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.