Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | Across Flow | ISO 294-4 | 1.1 | % |
| Modeling Shrinkage | 流量 | ISO 294-4 | 0.30 | % |
| Moisture Absorption | Saturation, 23°C, 2.00 mm | ISO 62 | 6.9 | % |
| Moisture Absorption | Equilibrium, 23°C, 2.00 mm, 50% RH | ISO 62 | 2.0 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Break | ISO 527-2 | 195 | Mpa |
| Tensile Strain | Break | ISO 527-2 | 3.5 | % |
| Tensile Modulus | | ISO 527-2 | 9800 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 260 | °C |
| Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 253 | °C |
| Linear thermal expansion coefficient | Flow | ISO 11359-2 | 2.8E-5 | cm/cm/°C |
| Linear thermal expansion coefficient | Across Flow | ISO 11359-2 | 9.5E-5 | cm/cm/°C |
| Glass Transition Temperature | | ISO 11357-2 | 80.0 | °C |
| Melting Temperature | | ISO 11357-3 | 262 | °C |
| Effective Thermal Diffusivity | | | 6.85E-8 | m²/s |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation Factor? | 100 Hz | IEC 62631-2-1 | 0.016 | |
| Dissipation Factor? | 1 MHz | IEC 62631-2-1 | 0.016 | |
| Comparative Tracking Index | 3.00 mm | UL 746 | PLC 0 | |
| Comparative Tracking Index | | IEC 60112 | 600 | V |
| Surface Resistivity | | IEC 62631-3-2 | -- | ohms |
| Volume Resistivity | | IEC 62631-3-1 | 1.0E+11 | ohms·m |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Density | | | 1.21 | g/cm³ |
| Specific Heat Capacity of Melt | | | 2290 | J/kg/°C |
| Thermal Conductivity of Melt | | | 0.21 | W/m/K |
| Odor | | VDA 270 | 4.50 | |
| Emission of Organic Compounds | | VDA 277 | 6.00 | µgC/g |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Temperature | | | 80 | °C |
| Drying time - Hot air dryer | | | 2.0 到 4.0 | hr |
| Suggested Max Moisture | | | 0.20 | % |
| Processing (Melt) Temp | | | 285 到 305 | °C |
| Melt Temperature, Optimum | | | 295 | °C |
| Mold Temperature | | | 70 到 120 | °C |
| Mold Temperature, Optimum | | | 100 | °C |
| Holding Pressure | | | 50.0 到 100 | Mpa |
| Holding Pressure | Drying Recommended | | yes | |
| Hold Pressure Time | | | 3.00 | s/mm |
| Maximum Screw Tangential Speed | | | 12 | m/min |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 60 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 80 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| atomization | F-value (refraction) | ISO 6452 | 95 | % |
| atomization | G-value (condensate) | ISO 6452 | 3.0E-4 | g |
| Burning Rate | 1.00 mm | ISO 3795 | 24 | mm/min |
| Flame Rating | 0.71 mm | UL 94, IEC 60695-11-10, -20 | HB | |
| Flame Rating | 1.5 mm | UL 94, IEC 60695-11-10, -20 | HB | |
| FMVSS Flammability | | FMVSS 302 | SE/B | |
| Oxygen Index | | ISO 4589-2 | 24 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.