Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD:3.00mm3 | % | 0.60到0.90 | -- |
| Modeling Shrinkage | MD:3.00mm4 | % | 0.20到0.50 | -- |
| Moisture Absorption | 23°C,24hr | % | 0.60 | -- |
| Moisture Absorption | Saturation,23°C | % | 4.0 | -- |
| Density / Specific Gravity | | ASTM D-792 | 无水｜1.59 | |
| Density / Specific Gravity | | ASTM D-792 | 1.3%水｜- | |
| Density / Specific Gravity | 23°C | g/cm³ | 1.59 | -- |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Taber Abrasion Resistance | 1000Cycles | mg | 26.0 | -- |
| Tensile Strength (Break) | 23℃ | ASTM D-638 | 无水｜1640 | kg/cm2 |
| Tensile Strength (Break) | 23℃ | ASTM D-638 | 1.3%水｜1350 | kg/cm2 |
| Tensile Stress | -40°C | MPa | 190 | -- |
| Tensile Stress | 23°C | MPa | 165 | |
| Tensile Stress | 80°C | MPa | 110 | -- |
| Tensile Strain | Break,-40°C | % | 2.5 | -- |
| Tensile Strain | Break,23°C | % | 3.0 | 3.0 |
| Tensile Strain | Break,80°C | % | 4.5 | -- |
| Tensile Elongation?(Break) | 23℃ | ASTM D-638 | 无水｜5 | % |
| Tensile Elongation?(Break) | 23℃ | ASTM D-638 | 1.3%水｜5 | % |
| Flexural Modulus | -40°C | MPa | 10200 | -- |
| Flexural Modulus | 23°C | MPa | 9300 | |
| Flexural Modulus | 80°C | MPa | 5500 | -- |
| Flexural Stress | -40°C | MPa | 275 | -- |
| Flexural Stress | 23°C | MPa | 250 | |
| Flexural Stress | 80°C | MPa | 150 | -- |
| Flexural strength | 23℃ | ASTM D-790 | 无水｜2490 | kg/cm2 |
| Flexural strength | 23℃ | ASTM D-790 | 1.3%水｜2000 | kg/cm2 |
| Flexural Modulus | 23℃ | ASTM D-790 | 无水｜93200 | kg/cm2 |
| Flexural Modulus | 23℃ | ASTM D-790 | 1.3%水｜65000 | kg/cm2 |
| Izod Impact Strength | 23℃，Unnotched1/8 | | 无水｜65 | kg.cm/cm |
| Izod Impact Strength | 23℃，Unnotched1/8 | | 1.3%水｜70 | kg.cm/cm |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear thermal expansion coefficient | MD | cm/cm/°C | 2E-05 | -- |
| Melting temperature | | °C | 265 | -- |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | °C | 251 | -- |
| Melting Temperature | | 差示扫描测热计DSC法 | 无水｜265 | °C |
| Melting Temperature | | 差示扫描测热计DSC法 | 1.3%水｜- | °C |
| Flame Rating | | UL 94 | 无水｜V-0 | |
| Flame Rating | | UL 94 | 1.3%水｜- | |
| Coefficient of Linear Thermal Expansion | | ASTM D-696 | 无水｜2 | 10-5cm/cm.℃ |
| Coefficient of Linear Thermal Expansion | | ASTM D-696 | 1.3%水｜- | |
| Deflection Temperature Under Load | 18.6kg/cm2 | ASTM D-648 | 无水｜251 | °C |
| Deflection Temperature Under Load | 18.6kg/cm2 | ASTM D-648 | 1.3%水｜- | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | | kV/mm | 38 | 33 |
| Dielectric Strength | 1/8" | ASTM D-149 | 无水｜38 | KV/mm |
| Dielectric Strength | 1/8" | ASTM D-149 | 1.3%水｜33 | KV/mm |
| Dielectric Constant | 23°C,1kHz | | 4.00 | -- |
| Dielectric Constant | 23°C,1MHz | | 0.0100 | -- |
| Arc Resistance | | sec | 70.0 | -- |
| Volume Resistivity | | ASTM D-257 | 无水｜8×1014 | Ω.cm |
| Volume Resistivity | | ASTM D-257 | 1.3%水｜8×1013 | Ω.cm |
| Volume Resistivity | | ohms·cm | 1E+15 | 1E+13 |
| Comparative Tracking Index | CTI | V | 200 | -- |
| Loss factor | 106Hz | ASTM D-150 | 无水｜0.003-0.009 | |
| Loss factor | 106Hz | ASTM D-150 | 1.3%水｜- | |
| Arc Resistance | 1/8" | ASTM D-495 | 无水｜70-80 | S |
| Arc Resistance | 1/8" | ASTM D-495 | 1.3%水｜- | S |
| Comparative Tracking Index | | UL 746 | 无水｜200 | V |
| Comparative Tracking Index | | UL 746 | 1.3%水｜- | V |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | kJ/m² | 65 | |
| Charpy Notched Impact Strength | -40°C | kJ/m² | 7.0 | -- |
| Charpy Notched Impact Strength | 23°C | kJ/m² | 9.5 | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Sale,23°C | | 121 | -- |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|
| Reinforcement Content | | | 无水｜30 | wt% |
| Reinforcement Content | | | 1.3%水｜- | wt% |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.40mm | | V-0 | -- |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 23℃，24hr | ASTM D-570 | 无水｜0.4 | % |
| Moisture Absorption | 23℃，24hr | ASTM D-570 | 1.3%水｜- | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.