Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD3.20mm | ASTMD995 | 0.55 | % |
| Density / Specific Gravity | | ASTMD792 | 1.18 | g/cm³ |
| Melt Mass-Flow Rate | 220℃/10Kg | ASTMD1238 | 53.00 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | 23°C | ASTMD256 | 280 | J/m |
| Notched Izod Impact Strength | -30°C | ASTMD256 | 78 | J/m |
| Tensile Elongation?(Break) | 23°C | ASTMD638 | 20 | % |
| Tensile Modulus | 23°C | ASTMD638 | 2160 | Mpa |
| Tensile Strength | 23°C | ASTMD638 | 42.2 | Mpa |
| Flexural Modulus | 23°C | ASTMD790 | 2550 | Mpa |
| Flexural Strength | 23°C | ASTMD790 | 69.6 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPaUnannealed | ASTMD648 | 84 | °C |
| Vicat Softening Temperature | | ASTM1525 | 84 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Insulation strength | | ASTMD149 | 27 | KV/mm |
| Volume Resistivity | | ASTMD257 | 1E+15 | Ω.cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | | ASTMD785 | 104 | R |
| Flame Rating | Test Condition | Test Method | Test Result | Unit |
|---|
| Fire rating | | UL-94 | 1.00mm | V-2 |
| Fire rating | | UL-94 | 1.50mm | V-1 |
| Fire rating | | UL-94 | 2.10mm | V-0,5VB |
| Fire rating | | UL-94 | 2.50mm | V-0,5VA |
| Fire rating | | UL-94 | 3.00mm | V-0,5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.